DuPont Performance Polymers Delrin® 520MP NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Delrin® 520MP NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
20% Teflon® Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Delrin 520MP is a medium viscosity acetal homopolymer containing 20% Teflon PTFE Micropowder. It is designed for applications requiring low wear and/or friction aInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.54 g/cc
0.0556 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Stress 32.4 MPa
<br>@Strain 1.80 %,<br> Temperature 23.0 °C
 4700 psi
<br>@Strain 1.80 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
33.3 MPa
<br>@Strain 1.10 %,<br> Temperature -40.0 °C
 4830 psi
<br>@Strain 1.10 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
38.4 MPa
<br>@Strain 1.70 %,<br> Temperature 0.000 °C
 5570 psi
<br>@Strain 1.70 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
49.2 MPa
<br>@Strain 7.10 %,<br> Temperature 23.0 °C
 7140 psi
<br>@Strain 7.10 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
50.2 MPa
<br>@Strain 12.4 %,<br> Temperature 23.0 °C
 7280 psi
<br>@Strain 12.4 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
50.6 MPa
<br>@Strain 17.8 %,<br> Temperature 23.0 °C
 7340 psi
<br>@Strain 17.8 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
57.2 MPa
<br>@Strain 6.90 %,<br> Temperature 0.000 °C
 8300 psi
<br>@Strain 6.90 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
58.2 MPa
<br>@Strain 12.1 %,<br> Temperature 0.000 °C
 8440 psi
<br>@Strain 12.1 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
58.5 MPa
<br>@Strain 17.3 %,<br> Temperature 0.000 °C
 8480 psi
<br>@Strain 17.3 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
68.5 MPa
<br>@Strain 4.20 %,<br> Temperature -40.0 °C
 9940 psi
<br>@Strain 4.20 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
72.6 MPa
<br>@Strain 7.40 %,<br> Temperature -40.0 °C
 10500 psi
<br>@Strain 7.40 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
73.6 MPa
<br>@Strain 10.5 %,<br> Temperature -40.0 °C
 10700 psi
<br>@Strain 10.5 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 53.0 MPa
7690 psi
ISO 527-1/-2
Elongation at Break 15 %
15 %
Nominal; ISO 527-1/-2
Elongation at Yield 13 %
13 %
ISO 527-1/-2
Tensile Modulus 2.80 GPa
406 ksi
ISO 527-1/-2
Flexural Modulus 2.70 GPa
392 ksi
ISO 178
Secant Modulus 0.354 GPa
<br>@Strain 6.30 %,<br> Temperature 100 °C
 51.3 ksi
<br>@Strain 6.30 %,<br> Temperature 212 °F
 ISO 11403-1 -2
0.354 GPa
<br>@Strain 14.2 %,<br> Temperature 23.0 °C
 51.4 ksi
<br>@Strain 14.2 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
0.419 GPa
<br>@Strain 13.9 %,<br> Temperature 0.000 °C
 60.8 ksi
<br>@Strain 13.9 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
0.441 GPa
<br>@Strain 6.80 %,<br> Temperature 80.0 °C
 64.0 ksi
<br>@Strain 6.80 %,<br> Temperature 176 °F
 ISO 11403-1 -2
0.600 GPa
<br>@Strain 3.10 %,<br> Temperature 100 °C
 87.0 ksi
<br>@Strain 3.10 %,<br> Temperature 212 °F
 ISO 11403-1 -2
0.693 GPa
<br>@Strain 7.10 %,<br> Temperature 23.0 °C
 101 ksi
<br>@Strain 7.10 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
0.747 GPa
<br>@Strain 3.40 %,<br> Temperature 80.0 °C
 108 ksi
<br>@Strain 3.40 %,<br> Temperature 176 °F
 ISO 11403-1 -2
0.829 GPa
<br>@Strain 6.90 %,<br> Temperature 0.000 °C
 120 ksi
<br>@Strain 6.90 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
0.850 GPa
<br>@Strain 0.800 %,<br> Temperature 100 °C
 123 ksi
<br>@Strain 0.800 %,<br> Temperature 212 °F
 ISO 11403-1 -2
0.870 GPa
<br>@Strain 8.40 %,<br> Temperature -40.0 °C
 126 ksi
<br>@Strain 8.40 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
1.07 GPa
<br>@Strain 0.900 %,<br> Temperature 80.0 °C
 155 ksi
<br>@Strain 0.900 %,<br> Temperature 176 °F
 ISO 11403-1 -2
1.63 GPa
<br>@Strain 4.20 %,<br> Temperature -40.0 °C
 237 ksi
<br>@Strain 4.20 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
1.80 GPa
<br>@Strain 1.80 %,<br> Temperature 23.0 °C
 261 ksi
<br>@Strain 1.80 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
2.26 GPa
<br>@Strain 1.70 %,<br> Temperature 0.000 °C
 328 ksi
<br>@Strain 1.70 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
3.03 GPa
<br>@Strain 1.10 %,<br> Temperature -40.0 °C
 439 ksi
<br>@Strain 1.10 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
ISO 179/1eA
0.400 J/cm²
<br>@Temperature -30.0 °C
 1.90 ft-lb/in²
<br>@Temperature -22.0 °F
 ISO 179/1eA
Tensile Creep Modulus, 1 hour 1500 MPa
<br>@Time 3600 sec
 218000 psi
<br>@Time 1.00 hour
 ISO 899-1
Tensile Creep Modulus, 1000 hours 800 MPa
<br>@Time 3.60e+6 sec
 116000 psi
<br>@Time 1000 hour
 ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 97.0 µm/m-°C
53.9 µin/in-°F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 94.0 °C
201 °F
ISO 75-1/-2
Flammability, UL94 HB
<br>@Thickness 1.50 mm
 HB
<br>@Thickness 0.0591 in
 IEC 60695-11-10
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Emission of organic compounds 7.5 µgC/g
VDA 277
Part Marking Code >POM-SD20<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification POM-SD20
ISO 1043
UL recognition UL