SABIC Innovative Plastics LNP Stat-kon EX08308C PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon EX08308C PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Stat-Kon* EX08308C is a high cleanliness Polyetherimide Compound reinforced with Carbon Fiber for use in applications requiring the highest level of cleanliness. This compound is compounded using LNP CCS Technology.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.387 g/cc | 0.05011 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.18 % @Time 86400 sec |
0.18 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0025 - 0.0031 cm/cm @Time 86400 sec |
0.0025 - 0.0031 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0036 - 0.0042 cm/cm @Time 86400 sec |
0.0036 - 0.0042 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 188 MPa | 27300 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 21.09 GPa | 3059 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 209 MPa | 30300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 16.0 GPa | 2320 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.500 J/cm @Temperature 23.0 °C |
0.937 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.09 J/cm @Temperature 23.0 °C |
5.79 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Impact Test | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 4.80 µm/m-°C @Temperature -40.0 - 40.0 °C |
2.67 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 44.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 6.40 mm |
392 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Flammability, UL94 | V-0 @Thickness 0.400 mm |
V-0 @Thickness 0.0157 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 25100 - 251000 ohm-cm | 25100 - 251000 ohm-cm | ASTM D 257 |
| Surface Resistance | 4500 - 90000 ohm | 4500 - 90000 ohm | ASTM D 257 |
| Static Decay | <= 0.10 sec | <= 0.10 sec | 5000V to <50V; FTMS101B |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY100FC PC+ABS (Asia Pacific)
- Fujipoly Industries Sarcon® GR-k Gap Filler Pad
- Ineos N00GX11 Polypropylene Impact Copolymer
- Hexcel® HexWeb® CR-PAA™ 5/32-5056-0.001 Phosphoric Acid Anodized Aluminum Honeycomb
- A. Schulman POLYBATCH™ White LL8970 TS Concentrate Based In LLDPE
- Chosun Refractories BPSC-95 Gas Purging Refractory
- Colorite Polymers CS1524SP Wire and Cable Insulation Vinyl Compound
- BASF Luranyl® KR 2403 G2 Polyphenylene Ether + Styrene-Butadiene Blend, 10% Glass Fiber Reinforced
- SABIC Innovative Plastics NORYL APS440 PPE+PPS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved