DuPont Performance Polymers Crastin® LW9330 BK851 PBT  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® LW9330 BK851 PBT  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Crastin® LW9330 BK851 is a 30% glass fiber reinforced, black polybutylene terephthalate alloy for injection molding. It has improved surface aesthetics, excellent dimensional stability and low warpage characteristics.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Filler Content 30 %
30 %
Mechanical Properties Metric English Comments
Tensile Strength at Break 133 MPa

@Temperature 23.0 °C
 19300 psi

@Temperature 73.4 °F
 ISO 527
Tensile Stress 5.18 MPa

@Strain 0.100 %,
Temperature 100 °C
 751 psi

@Strain 0.100 %,
Temperature 212 °F
 ISO 11403-1/-2
7.49 MPa

@Strain 0.100 %,
Temperature 80.0 °C
 1090 psi

@Strain 0.100 %,
Temperature 176 °F
 ISO 11403-1/-2
8.17 MPa

@Strain 0.100 %,
Temperature 23.0 °C
 1180 psi

@Strain 0.100 %,
Temperature 73.4 °F
 ISO 11403-1/-2
9.44 MPa

@Strain 0.100 %,
Temperature -40.0 °C
 1370 psi

@Strain 0.100 %,
Temperature -40.0 °F
 ISO 11403-1/-2
9.51 MPa

@Strain 0.200 %,
Temperature 100 °C
 1380 psi

@Strain 0.200 %,
Temperature 212 °F
 ISO 11403-1/-2
13.08 MPa

@Strain 0.300 %,
Temperature 100 °C
 1897 psi

@Strain 0.300 %,
Temperature 212 °F
 ISO 11403-1/-2
14.75 MPa

@Strain 0.200 %,
Temperature 80.0 °C
 2139 psi

@Strain 0.200 %,
Temperature 176 °F
 ISO 11403-1/-2
17.33 MPa

@Strain 0.200 %,
Temperature 23.0 °C
 2514 psi

@Strain 0.200 %,
Temperature 73.4 °F
 ISO 11403-1/-2
18.94 MPa

@Strain 0.200 %,
Temperature -40.0 °C
 2747 psi

@Strain 0.200 %,
Temperature -40.0 °F
 ISO 11403-1/-2
20.38 MPa

@Strain 0.500 %,
Temperature 100 °C
 2956 psi

@Strain 0.500 %,
Temperature 212 °F
 ISO 11403-1/-2
20.83 MPa

@Strain 0.300 %,
Temperature 80.0 °C
 3021 psi

@Strain 0.300 %,
Temperature 176 °F
 ISO 11403-1/-2
23.72 MPa

@Strain 0.600 %,
Temperature 100 °C
 3440 psi

@Strain 0.600 %,
Temperature 212 °F
 ISO 11403-1/-2
26.42 MPa

@Strain 0.300 %,
Temperature 23.0 °C
 3832 psi

@Strain 0.300 %,
Temperature 73.4 °F
 ISO 11403-1/-2
26.52 MPa

@Strain 0.700 %,
Temperature 100 °C
 3846 psi

@Strain 0.700 %,
Temperature 212 °F
 ISO 11403-1/-2
28.75 MPa

@Strain 0.800 %,
Temperature 100 °C
 4170 psi

@Strain 0.800 %,
Temperature 212 °F
 ISO 11403-1/-2
28.9 MPa

@Strain 0.300 %,
Temperature -40.0 °C
 4190 psi

@Strain 0.300 %,
Temperature -40.0 °F
 ISO 11403-1/-2
30.54 MPa

@Strain 0.900 %,
Temperature 100 °C
 4429 psi

@Strain 0.900 %,
Temperature 212 °F
 ISO 11403-1/-2
32.05 MPa

@Strain 0.500 %,
Temperature 80.0 °C
 4648 psi

@Strain 0.500 %,
Temperature 176 °F
 ISO 11403-1/-2
32.16 MPa

@Strain 1.00 %,
Temperature 100 °C
 4664 psi

@Strain 1.00 %,
Temperature 212 °F
 ISO 11403-1/-2
33.48 MPa

@Strain 1.10 %,
Temperature 100 °C
 4856 psi

@Strain 1.10 %,
Temperature 212 °F
 ISO 11403-1/-2
34.63 MPa

@Strain 1.20 %,
Temperature 100 °C
 5023 psi

@Strain 1.20 %,
Temperature 212 °F
 ISO 11403-1/-2
35.64 MPa

@Strain 1.30 %,
Temperature 100 °C
 5169 psi

@Strain 1.30 %,
Temperature 212 °F
 ISO 11403-1/-2
36.35 MPa

@Strain 0.600 %,
Temperature 80.0 °C
 5272 psi

@Strain 0.600 %,
Temperature 176 °F
 ISO 11403-1/-2
36.46 MPa

@Strain 1.40 %,
Temperature 100 °C
 5288 psi

@Strain 1.40 %,
Temperature 212 °F
 ISO 11403-1/-2
37.08 MPa

@Strain 1.50 %,
Temperature 100 °C
 5378 psi

@Strain 1.50 %,
Temperature 212 °F
 ISO 11403-1/-2
37.65 MPa

@Strain 1.60 %,
Temperature 100 °C
 5461 psi

@Strain 1.60 %,
Temperature 212 °F
 ISO 11403-1/-2
38.11 MPa

@Strain 1.70 %,
Temperature 100 °C
 5527 psi

@Strain 1.70 %,
Temperature 212 °F
 ISO 11403-1/-2
38.57 MPa

@Strain 1.80 %,
Temperature 100 °C
 5594 psi

@Strain 1.80 %,
Temperature 212 °F
 ISO 11403-1/-2
39.06 MPa

@Strain 1.90 %,
Temperature 100 °C
 5665 psi

@Strain 1.90 %,
Temperature 212 °F
 ISO 11403-1/-2
39.51 MPa

@Strain 2.00 %,
Temperature 100 °C
 5730 psi

@Strain 2.00 %,
Temperature 212 °F
 ISO 11403-1/-2
39.99 MPa

@Strain 2.10 %,
Temperature 100 °C
 5800 psi

@Strain 2.10 %,
Temperature 212 °F
 ISO 11403-1/-2
40.07 MPa

@Strain 0.700 %,
Temperature 80.0 °C
 5812 psi

@Strain 0.700 %,
Temperature 176 °F
 ISO 11403-1/-2
40.44 MPa

@Strain 2.20 %,
Temperature 100 °C
 5865 psi

@Strain 2.20 %,
Temperature 212 °F
 ISO 11403-1/-2
40.83 MPa

@Strain 2.30 %,
Temperature 100 °C
 5922 psi

@Strain 2.30 %,
Temperature 212 °F
 ISO 11403-1/-2
41.13 MPa

@Strain 2.40 %,
Temperature 100 °C
 5965 psi

@Strain 2.40 %,
Temperature 212 °F
 ISO 11403-1/-2
41.41 MPa

@Strain 2.50 %,
Temperature 100 °C
 6006 psi

@Strain 2.50 %,
Temperature 212 °F
 ISO 11403-1/-2
41.65 MPa

@Strain 2.60 %,
Temperature 100 °C
 6041 psi

@Strain 2.60 %,
Temperature 212 °F
 ISO 11403-1/-2
41.86 MPa

@Strain 2.70 %,
Temperature 100 °C
 6071 psi

@Strain 2.70 %,
Temperature 212 °F
 ISO 11403-1/-2
42.05 MPa

@Strain 2.80 %,
Temperature 100 °C
 6099 psi

@Strain 2.80 %,
Temperature 212 °F
 ISO 11403-1/-2
42.21 MPa

@Strain 2.90 %,
Temperature 100 °C
 6122 psi

@Strain 2.90 %,
Temperature 212 °F
 ISO 11403-1/-2
42.33 MPa

@Strain 3.90 %,
Temperature 100 °C
 6139 psi

@Strain 3.90 %,
Temperature 212 °F
 ISO 11403-1/-2
42.37 MPa

@Strain 3.00 %,
Temperature 100 °C
 6145 psi

@Strain 3.00 %,
Temperature 212 °F
 ISO 11403-1/-2
42.48 MPa

@Strain 3.10 %,
Temperature 100 °C
 6161 psi

@Strain 3.10 %,
Temperature 212 °F
 ISO 11403-1/-2
42.59 MPa

@Strain 3.20 %,
Temperature 100 °C
 6177 psi

@Strain 3.20 %,
Temperature 212 °F
 ISO 11403-1/-2
42.63 MPa

@Strain 3.80 %,
Temperature 100 °C
 6183 psi

@Strain 3.80 %,
Temperature 212 °F
 ISO 11403-1/-2
42.66 MPa

@Strain 3.30 %,
Temperature 100 °C
 6187 psi

@Strain 3.30 %,
Temperature 212 °F
 ISO 11403-1/-2
42.71 MPa

@Strain 3.40 %,
Temperature 100 °C
 6195 psi

@Strain 3.40 %,
Temperature 212 °F
 ISO 11403-1/-2
42.71 MPa

@Strain 3.70 %,
Temperature 100 °C
 6195 psi

@Strain 3.70 %,
Temperature 212 °F
 ISO 11403-1/-2
42.75 MPa

@Strain 3.50 %,
Temperature 100 °C
 6200 psi

@Strain 3.50 %,
Temperature 212 °F
 ISO 11403-1/-2
42.75 MPa

@Strain 3.60 %,
Temperature 100 °C
 6200 psi

@Strain 3.60 %,
Temperature 212 °F
 ISO 11403-1/-2
43.98 MPa

@Strain 0.800 %,
Temperature 80.0 °C
 6379 psi

@Strain 0.800 %,
Temperature 176 °F
 ISO 11403-1/-2
44.12 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 6399 psi

@Strain 0.500 %,
Temperature 73.4 °F
 ISO 11403-1/-2
47.48 MPa

@Strain 0.900 %,
Temperature 80.0 °C
 6886 psi

@Strain 0.900 %,
Temperature 176 °F
 ISO 11403-1/-2
50.0 MPa

@Strain 0.500 %,
Temperature -40.0 °C
 7250 psi

@Strain 0.500 %,
Temperature -40.0 °F
 ISO 11403-1/-2
50.45 MPa

@Strain 1.00 %,
Temperature 80.0 °C
 7317 psi

@Strain 1.00 %,
Temperature 176 °F
 ISO 11403-1/-2
53.04 MPa

@Strain 1.10 %,
Temperature 80.0 °C
 7693 psi

@Strain 1.10 %,
Temperature 176 °F
 ISO 11403-1/-2
54.45 MPa

@Strain 0.600 %,
Temperature 23.0 °C
 7897 psi

@Strain 0.600 %,
Temperature 73.4 °F
 ISO 11403-1/-2
55.36 MPa

@Strain 1.20 %,
Temperature 80.0 °C
 8029 psi

@Strain 1.20 %,
Temperature 176 °F
 ISO 11403-1/-2
57.42 MPa

@Strain 1.30 %,
Temperature 80.0 °C
 8328 psi

@Strain 1.30 %,
Temperature 176 °F
 ISO 11403-1/-2
59.16 MPa

@Strain 1.40 %,
Temperature 80.0 °C
 8580 psi

@Strain 1.40 %,
Temperature 176 °F
 ISO 11403-1/-2
59.58 MPa

@Strain 0.600 %,
Temperature -40.0 °C
 8641 psi

@Strain 0.600 %,
Temperature -40.0 °F
 ISO 11403-1/-2
60.64 MPa

@Strain 1.50 %,
Temperature 80.0 °C
 8795 psi

@Strain 1.50 %,
Temperature 176 °F
 ISO 11403-1/-2