Multibase Multi-FlexÂ® A 9002 MR TPE Thermoplastic Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	Multibase
Trade Name	Multi-Flex®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Multibase Multi-FlexÂ® A 9002 MR TPE Thermoplastic Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Features: Chemical Resistance, Good Colorability, GoodElasticity, HighElectrically InsulatingFlame RetardantFlexibility, GoodHeat StabilizedOzone ResistantProcessability, GoodUV Resistance, Good Scratch Resistant Forms:PelletsProcessing Method:Injection Molding Information provided by Multibase

Physical Properties	Metric	English	Comments
Specific Gravity	0.920 g/cc	0.920 g/cc	ASTM 792
Linear Mold Shrinkage	0.015 cm/cm	0.015 in/in	ASTM D955
Melt Flow	4.0 g/10 min @Load 2.16 kg, Temperature 230 Â°C	4.0 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	90	90	10 seconds; ASTM D2240
Tensile Strength, Ultimate	10.3 MPa	1500 psi	ASTM D638
Elongation at Break	680 %	680 %	ASTM D638
Flexural Modulus	1.14 GPa	165 ksi	1% Secant; ASTM D790
Tear Strength	70.1 kN/m	400 pli	ASTM D624

Thermal Properties	Metric	English	Comments
Brittleness Temperature	-50.0 Â°C	-58.0 Â°F	ASTM D746
Flame Spread	19 mm/min	0.75 in/min	FM VSS-302
	19 mm/min	0.75 in/min	VSS 302

Processing Properties	Metric	English
Middle Barrel Temperature	210 Â°C	410 Â°F
Front Barrel Temperature	227 Â°C	440 Â°F
Nozzle Temperature	235 Â°C	455 Â°F
Mold Temperature	51.7 Â°C	125 Â°F
Drying Temperature	51.7 Â°C	125 Â°F
Dry Time	2 - 4 hour	2 - 4 hour
Injection Pressure	3.45 - 4.83 MPa	500 - 700 psi
Back Pressure	0.345 MPa	50.0 psi
Screw Speed	40 rpm	40 rpm

Descriptive Properties	Value	Comments
Clamp Tonnage	1.5-2.5 tons/in²
Fogging	Min. 90	SAE-J275
Injection Rate	Fast
Suggested Max Regrind	0.5