DuPont Elvaloy® 3117 AC Ethylene and 17% Butyl Acrylate Copolymer
| Category | Polymer , Film , Thermoplastic , Ethylene Butyl Acrylate |
| Manufacturer | DuPont Packaging and Industrial Polymers |
| Trade Name | Elvaloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Elvaloy® 3117 AC Ethylene and 17% Butyl Acrylate Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Elvaloy® 3117 AC is intended for coextrusion and compounding. Due to its high melt flow rate, it is used also in extrusion coating. Elvaloy® 3117 AC is soft, flexible and has good adhesion to various polymers. It combines high melting point and good sealing properties.Elvaloy® 3117 AC is easily processed on standard equipment used for low density polyethylene. EBA polymers show excellent thermal stability, which allows higher processing temperatures, if needed.Information provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D792 - ISO 1183 |
| Melt Flow | 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 90 | 90 | ASTM D2240 - ISO 868 |
| Hardness, Shore D | 32 | 32 | ASTM D2240 - ISO 868 |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
| Elongation at Break | 800 % | 800 % | 500 mm/min; ASTM D638 - ISO 527-2 |
| Tensile Modulus | 0.0400 GPa | 5.80 ksi | 1 mm/min; ASTM D638 - ISO 527-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 99.0 °C | 210 °F | By DSC; ASTM D3418 - ISO 3146 |
| Vicat Softening Point | 60.0 °C | 140 °F | A<sub>50</sub> (10N); ASTM D1525 - ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 150 °C | 302 °F | Extrusion lamination and extrusion coating |
| 150 °C | 302 °F | Cast film | |
| 150 °C | 302 °F | Blown film | |
| Middle Barrel Temperature | 160 °C | 320 °F | Blown film |
| 210 °C | 410 °F | Cast film | |
| 220 °C | 428 °F | Extrusion lamination | |
| Front Barrel Temperature | 170 °C | 338 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Adapter Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast Film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Die Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Melt Temperature | 150 °C | 302 °F | For film extrusion |
| Descriptive Properties | Value | Comments |
|---|---|---|
| BA-Content | 17 wt.% | DuPont Method |
Users viewing this material also viewed the following:
- Overview of materials for PVC, 10% Glass Fiber Reinforced
- LyondellBasell Petrothene® NA340185 Low Density Polyethylene, Film Extrusion Grade
- Techmer ES Elastoblend® PBT E IM SL3
- Techmer ES HiFill FR® HDPE E FR
- Teknor Apex APEX® 4103 Polyvinyl Chloride, Flexible
- Shin-Etsu Silicones LIMSâ„¢ KE2004-10A/B Elastomer
- Washington Penn High Modulus Polypropylene Homopolymer 40% Glass Filled
- ExxonMobil Santoprene® 251-92W232 Thermoplastic Elastomer
- 3M Cushion-Mount™ 1920S Plus Plate Mounting Tape
- Ascend Performance Materials Vydyne® 75HF Nylon 66/6, Heat Stabilized, Conditioned
Copyright © lookpolymers.com All Rights Reserved