Techmer ES LuriblendÂ® PA6/6 M/TL7 HS L Nylon 66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized , Nylon 66, PTFE Filled
Manufacturer	Techmer ES
Trade Name	Luriblend®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Techmer ES LuriblendÂ® PA6/6 M/TL7 HS L Nylon 66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Lubricant, PTFE Lubricant and Molybdenum Disulfide LubricantFeatures: Lubricated and Heat StabilizerProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.

Physical Properties	Metric	English	Comments
Density	1.18 g/cc	0.0426 lb/inÂ³	ASTM D792
Water Absorption	1.0 % @Time 86400 sec	1.0 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.015 cm/cm @Thickness 3.17 mm	0.015 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	117	117	ASTM D785
Tensile Strength	73.1 MPa	10600 psi	ASTM D638
Elongation at Yield	20 %	20 %	ASTM D638
Flexural Yield Strength	101 MPa	14700 psi	ASTM D790
Flexural Modulus	2.76 GPa	400 ksi	ASTM D790
Izod Impact, Notched	0.427 J/cm @Thickness 3.17 mm	0.800 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	79.2 Âµm/m-Â°C	44.0 Âµin/in-Â°F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	93.3 Â°C	200 Â°F	Unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	ASTM D257
Dielectric Strength	21.7 kV/mm	550 kV/in	Method A (Short-Time); ASTM D149