SABIC Innovative Plastics LNP STAT-KON DX04462C PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX04462C PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DX04462C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ASTM D638 |
| 53.0 MPa | 7690 psi | ISO 527 | |
| Elongation at Break | 5.7 % | 5.7 % | ISO 527 |
| 7.4 % | 7.4 % | ASTM D638 | |
| Tensile Modulus | 2.47 GPa | 358 ksi | 50 mm/min; ASTM D638 |
| 2.56 GPa | 371 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| 98.0 MPa | 14200 psi | ISO 178 | |
| Flexural Modulus | 2.71 GPa | 393 ksi | ASTM D790 |
| 2.72 GPa | 395 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.78 J/cm | 12.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 68.0 kJ/m² | 32.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 63.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 61.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 62.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+6 - 1.00e+9 ohm | 1.00e+6 - 1.00e+9 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Overview of materials for PVC/Acrylic Alloy
- Hexion Bakelite™ PF 38110 Phenolic Formaldehyde Resin, High Surface Quality (discontinued **)
- Fainplast Compounds RH 4410 Rigid PVC, Antishock Extrusion
- Garlock 2930 Compressed Aramid Fiber Gasketing, Neoprene Binder
- American Elements Manganese Nanoparticles
- Hippe PF CC 33 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod
- Ashley Polymers Ashlene® P114WO PBT Polyester
- BASF Sicotan® Yellow L 1912 Color Additive
- Arkema Group Oroglas® V 044 Acrylic, Extrusion Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved