Dow ELITE™ 5400G Enhanced Polyethylene Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Dow Chemical
Trade Name ELITE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow ELITE™ 5400G Enhanced Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
™ 5400G is a copolymer produced via INSITE™ Technology from Dow Plastics. It offers a unique combination of low seal initiation, moderate stiffness and low blocking tendencies for good performance on automated packaging equipment. ELLITE™ 5400G resin complies with U.S. FDA regulation 21 CFR 177.1520 (c) 3.2a.Information provided by Dow
Physical Properties Metric English Comments
Density 0.916 g/cc
0.0331 lb/in³
ASTM D792
Thickness 50.8 microns
2.00 mil
Melt Flow 1.0 g/10 min
1.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.818 MPa
1424 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.17 MPa
1475 psi
ASTM D882
Film Elongation at Break, MD 609 %
609 %
ASTM D882
Film Elongation at Break, TD 671 %
671 %
ASTM D882
Secant Modulus, MD 0.1658 GPa
24.05 ksi
2% Secant; ASTM D882
Secant Modulus, TD 0.1912 GPa
27.73 ksi
2% Secant; ASTM D882
Impact 27
27
[lb<sub>f</sub>]; Puncture Resistance Force; Dow Method
334
334
[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
Puncture Energy 11.9 J
8.75 ft-lb
Dow Method
Elmendorf Tear Strength MD 825 g
825 g
ASTM D1922
Elmendorf Tear Strength TD 1014 g
1014 g
ASTM D1922
Elmendorf Tear Strength, MD 16.24 g/micron
412.5 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 20.0 g/micron
507 g/mil
ASTM D1922
Dart Drop Test >= 850 g
>= 1.87 lb
Method B; ASTM D1709
Film Tensile Strength at Break, MD 56.85 MPa
8246 psi
ASTM D882
Film Tensile Strength at Break, TD 52.84 MPa
7664 psi
ASTM D882
Heat Seal Strength Initiation Temperature 99.0 °C
210 °F
2 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method
Thermal Properties Metric English Comments
Melting Point 123 °C
253 °F
Dow Method (DSC)
Vicat Softening Point 101 °C
214 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 9.0 %
9.0 %
ASTM D1003
Gloss 70 %
70 %
45°; ASTM D2457