Carmel Olefins CAPILENE® T 89 E Polypropylene Homopolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Fiber Grade
Manufacturer	Carmel Olefins
Trade Name	CAPILENE®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Carmel Olefins CAPILENE® T 89 E Polypropylene Homopolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: CAPILENE® T 89 E is a high melt flow rate homopolymer for continuous filaments, staple fibers and for injection molding. It is formulated with an anti-gasfading stabilization package. It exhibits good stiffness and toughness balance, combined with good processabilityApplications: CAPILENE® T 89 E is suitable for gasfading resistance continuous filaments (BCF & CF), for gasfading resistance staple fibers and injection molding of household articles, closures, crates, containers and garden furniture.Information provided by Carmel Olefins.

Physical Properties	Metric	English	Comments
Melt Flow	25 g/10 min @Load 2.16 kg, Temperature 230 °C	25 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	32.0 MPa	4640 psi	50 mm/min; ASTM D638
Elongation at Yield	12 %	12 %	50 mm/min; ASTM D638
Flexural Modulus	1.45 GPa	210 ksi	ASTM D790
Izod Impact, Notched	0.250 J/cm	0.468 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	97.0 °C	207 °F	ASTM D648
Vicat Softening Point	155 °C @Load 1.02 kg	311 °F @Load 2.25 lb	ASTM D1525