Dow DOWLEX™ 2037 Linear Low Density Polyethylene, Cast Film Grade

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer	Dow Chemical
Trade Name	DOWLEX™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow DOWLEX™ 2037 Linear Low Density Polyethylene, Cast Film Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

DOWLEX® 2037 Polyethylene is a cast film extrusion resin for high stiffness film applications. It complies with U.S. FDA regulation 21 CFR 177.1520 c 3.2a when used unmodified and according to good manufacturing practices for food contact applications. The regulation should be consulted for complete details.Film properties below based on a film thickness of 30 µm. Data provided by Dow Chemical.

Physical Properties	Metric	English	Comments
Density	0.935 g/cc	0.0338 lb/in³
Thickness	30.0 microns	1.18 mil
Melt Flow	2.5 g/10 min @Load 2.16 kg	2.5 g/10 min @Load 4.76 lb	Melt flow ratio I10/I2 is 7.2.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	18.3 MPa	2650 psi	Molded property
Film Tensile Strength at Yield, MD	15.2 MPa	2200 psi
Film Tensile Strength at Yield, TD	18.6 MPa	2700 psi
Tensile Strength, Yield	20.0 MPa	2900 psi	Molded property
Film Elongation at Break, MD	420 %	420 %
Film Elongation at Break, TD	460 %	460 %
Elongation at Break	400 %	400 %	Molded value
Elmendorf Tear Strength MD	70 g	70 g
Elmendorf Tear Strength TD	470 g	470 g
Elmendorf Tear Strength, MD	2.30 g/micron	58.4 g/mil
Elmendorf Tear Strength, TD	15.7 g/micron	399 g/mil
Dart Drop	1.70 g/micron	43.2 g/mil
Film Tensile Strength at Break, MD	35.2 MPa	5110 psi
Film Tensile Strength at Break, TD	31.0 MPa	4500 psi

Optical Properties	Metric	English	Comments
Haze	3.5 %	3.5 %
Gloss	85 %	85 %	45°

Processing Properties	Metric	English	Comments
Processing Temperature	274 °C	525 °F	Film extrusion temperature