| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Plating Grade |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS 3003 MC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: High Heat Plating GradeInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.055 g/cc | 1.055 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 1.2 g/10 min @Load 10.0 kg, Temperature 220 °C |
1.2 g/10 min @Load 22.0 lb, Temperature 428 °F |
Procedure A; ASTM D1238 |
| 4.2 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.2 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Yield | 42.46 MPa | 6158 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.34 GPa | 339 ksi | Procedure B, Test Method I(chs 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 2.83 J/cm | 5.30 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 83.9 °C | 183 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| 91.1 °C | 196 °F | 0.25 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 | |
| Vicat Softening Point | 115 °C | 239 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 7.58 MPa | 700 - 1100 psi |
Users viewing this material also viewed the following:
- Nye Lubricants 176F (SO) Synthetic Oil
- Eastman Tenite 383A-08 Cellulose Acetate Propionate (discontinued **)
- Solvay Specialty Polymers Ryton® XE5030BL Polyphenylene Sulfide Alloy (PPS Alloy), 30% Glass Fiber
- A. Schulman POLYBATCH™ Blue 4020 Concentrate Based In Polyethylene
- Loctite® 312 Acrylic Bonding Adhesive
- ExxonMobil LD 071.LR Blown Film Resin
- ExxonMobil SAE 40 Mobilgard M40 Series
- 3M 7028FL Screen Printable Polyester Performance LabelProducts
Copyright © lookpolymers.com All Rights Reserved