DSM Stanyl® TE350 Nylon 46 (European and Asian Grade) (Dry) (discontinued **)

Category	Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Unreinforced
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DSM Stanyl® TE350 Nylon 46 (European and Asian Grade) (Dry) (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Stanyl is a high performance polyamide providing unmatched performance and value across an amazingly broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temperatures Excellent resistance to wear and low friction Outstanding flow for easy processing and exceptional design freedomStanyl High Flowgrades that match the best flowing LCPs while maintaining a high level of mechanical propertiesKey Applications: Automotive: Powertrain components, Charge-air coolers, EPS and ETC gears, Motor Sensors, Auto connectors, Chain tensionersE&E: Connectors, Microswitches, Bobbins, Memory modules, Motor components, Industrial, Specialty films and fibers, Consumer appliancesInformation provided by DSM.

Physical Properties	Metric	English	Comments
Density	1.38 g/cc	0.0499 lb/in³	ISO 1183
Water Absorption	9.5 %	9.5 %	Sim. to ISO 62
Moisture Absorption at Equilibrium	2.6 %	2.6 %	Humidity Absorption; Sim. to ISO 62
Viscosity Test	185 cm³/g	185 cm³/g	Viscosity Number
Linear Mold Shrinkage, Flow	0.020 cm/cm	0.020 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.020 cm/cm	0.020 in/in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	85.0 MPa	12300 psi	ISO 527-1/-2
Elongation at Break	20 %	20 %	ISO 527-1/-2
Elongation at Yield	5.0 %	5.0 %	ISO 527-1/-2
Tensile Modulus	3.60 GPa	522 ksi	ISO 527-1/-2
Charpy Impact Unnotched	10.0 J/cm² @Temperature -30.0 °C	47.6 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	10.0 J/cm² @Temperature 23.0 °C	47.6 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.400 J/cm² @Temperature -30.0 °C	1.90 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.600 J/cm² @Temperature 23.0 °C	2.86 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	80.0 µm/m-°C @Temperature 20.0 °C	44.4 µin/in-°F @Temperature 68.0 °F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	90.0 µm/m-°C @Temperature 20.0 °C	50.0 µin/in-°F @Temperature 68.0 °F	ISO 11359-1/-2
Melting Point	295 °C	563 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	275 °C	527 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	190 °C	374 °F	ISO 75-1/-2
Vicat Softening Point	280 °C	536 °F	50°C/h 50N; ISO 306
Glass Transition Temp, Tg	75.0 °C	167 °F	Glass Transition Temperature (10°C/min); ISO 11357-1/-2
Flammability, UL94	V-0 @Thickness 0.750 mm	V-0 @Thickness 0.0295 in	IEC 60695-11-10
	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in	IEC 60695-11-10
Oxygen Index	29 %	29 %	ISO 4589-1/-2
Glow Wire Test	825 °C @Thickness 0.750 mm	1520 °F @Thickness 0.0295 in	Glow Wire Ignition Temperature; IEC 60695-2-13
	825 °C @Thickness 3.00 mm	1520 °F @Thickness 0.118 in	Glow Wire Ignition Temperature; IEC 60695-2-13
	960 °C @Thickness 0.750 mm	1760 °F @Thickness 0.0295 in	Glow Wire Flammability Index; IEC 60695-2-12
	960 °C @Thickness 3.00 mm	1760 °F @Thickness 0.118 in	Glow Wire Flammability Index; IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	IEC 60093
Dielectric Constant	3.5 @Frequency 1e+6 Hz	3.5 @Frequency 1e+6 Hz	IEC 60250
	3.8 @Frequency 100 Hz	3.8 @Frequency 100 Hz	IEC 60250
Dielectric Strength	30.0 kV/mm	762 kV/in	IEC 60243-1
Dissipation Factor	0.00050 @Frequency 100 Hz	0.00050 @Frequency 100 Hz	IEC 60250
	0.0020 @Frequency 1e+6 Hz	0.0020 @Frequency 1e+6 Hz	IEC 60250
Comparative Tracking Index	325 V	325 V	IEC 60112

Descriptive Properties	Value	Comments
Flame Retardant	Yes
Flame Retarding Agent	Yes
Heat stabilized or stable to heat	Yes
Injection molding	Yes
Lubricants	Yes
Platable	Yes
Release Agent	Yes
Without Fillers	Yes