Lehmann & Voss LUVOCOM® 1105/GF/40/BK-1 PEEK, with glass fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105/GF/40/BK-1 PEEK, with glass fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; impact resistance.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts, high continuous use temperature.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 180 MPa | 26100 psi | |
| Elongation at Yield | 2.0 % | 2.0 % | |
| 2.5 % | 2.5 % | flexural | |
| Modulus of Elasticity | 13.0 GPa | 1890 ksi | |
| Flexural Strength | 250 MPa | 36300 psi | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | |
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Coefficient of Friction, Dynamic | 0.31 | 0.31 | |
| Coefficient of Friction, Static | 0.29 | 0.29 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 280 °C | 536 °F | short term | |
| Vicat Softening Point | 325 °C | 617 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable EHA70L Polyvinyl Chloride, Flexible (PVC, Flexible)
- NCMT NanoPAC™ HS402 High Performance Polypropylene Nanocomposite
- Kotec Carbotex K-40MRA Polycarbonate, General Purpose, Mold Release Grade
- Samsung Cheil Industries Starex® NA-0660I ABS, Unreinforced Anti-Bacteria Grade
- ThyssenKrupp PAS 550 Structural Steel for Cold Forming
- ThyssenKrupp PAS 700 Structural Steel for Cold Forming
- Dow Corning HMW 2220 Non-Ionic Emulsion
- Diamond Polymers ASA 91802
- Abatron AboCast 8103-28 High-Performance Dielectric Epoxy
- Zeon Chemicals Quintac® 3280 SIS Rubber
Copyright © lookpolymers.com All Rights Reserved