SABIC Innovative Plastics LNP THERMOCOMP WZ002 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP WZ002 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* WZ002 is a compound based on PBT resin containing 10% Milled Glass.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Water Absorption 0.10 %

@Time 86400 sec
 0.10 %

@Time 24.0 hour
 ISO 62-1
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
5 mm/min; ISO 527
Tensile Strength, Yield 47.0 MPa
6820 psi
5 mm/min; ISO 527
Elongation at Break 2.4 %
2.4 %
5 mm/min; ISO 527
Elongation at Yield 2.3 %
2.3 %
5 mm/min; ISO 527
Tensile Modulus 5.00 GPa
725 ksi
1 mm/min; ISO 527
Flexural Strength 85.0 MPa
12300 psi
2 mm/min; ISO 178
Flexural Modulus 2.90 GPa
421 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 149 °C
300 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 64.0 °C
147 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af