SABIC Innovative Plastics NORYL WCP761 PPE-TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCP761 PPE-TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flexible Noryl injection molding grade. Low specific gravity with very good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain relief""s, and connectors. UL94 V-0 performance with good processability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Time 173000 sec |
0.10 % @Time 48.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0108 cm/cm @Time 86400 sec |
0.0108 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Flow | 14.5 g/10 min @Load 5.00 kg, Temperature 210 °C |
14.5 g/10 min @Load 11.0 lb, Temperature 410 °F |
ASTM D1238 |
| 20 g/10 min @Load 2.16 kg, Temperature 250 °C |
20 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 78 | 78 | 30S reading; ASTM D2240 |
| Tensile Strength at Break | 7.00 MPa | 1020 psi | Type I, 50 mm/min; ASTM D638 |
| 8.00 MPa | 1160 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 165 % | 165 % | Type I, 50 mm/min; ASTM D638 |
| 165 % | 165 % | 50 mm/min; ISO 527 | |
| Flexural Modulus | 0.0400 GPa | 5.80 ksi | 12.5 mm/min; ISO 178 |
| 0.0500 GPa | 7.25 ksi | 12.5 mm/min, 100 mm span; ASTM D790 | |
| Tear Strength | 16.0 kN/m | 91.3 pli | ISO 6383 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
| Flammability, UL94 | V-0 @Thickness 6.00 mm |
V-0 @Thickness 0.236 in |
UL 94 |
| Oxygen Index | 24 % | 24 % | ISO 4589 |
| Glow Wire Test | 775 °C | 1430 °F | IEC 60695-2-13 |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.30e+16 ohm-cm | 1.30e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.5 @Frequency 1.00e+6 Hz |
2.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® SOL B 183 Styrene - Butadiene Copolymer
- Kolon KOPA® KN173HI2 High Impact Nylon 6
- LG Chemical LUPOY HP5004 PC/ABS, High Impact at Low Temperature
- Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled
- SABIC Innovative Plastics LNP THERMOTUF R1000I PA 66
- Total PSI 7240 High Impact Polystyrene
- Cossa Polimeri ESTACARB 0820 GF V0-5V Flame Retardant Polycarbonate
- CP-Polymer-Technik Wellamid® 6000/58 GV 15 HWUVCP 15% Glass Fiber Nylon 6, Impact Modified Until -40°C, UV Stabilized, Heat Stabilized, Conditioned
Copyright © lookpolymers.com All Rights Reserved