Covestro Makrolon® 3107 MAS167 Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded , Polycarbonate, UV Stabilized |
| Manufacturer | Covestro |
| Trade Name | Makrolon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Makrolon® 3107 MAS167 Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• High viscosity, easy release• UV stabilizedAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.660 g/cc | 0.0238 lb/in³ | pellets; ISO 60 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183-1 |
| Moisture Absorption at Equilibrium | 0.12 % | 0.12 % | ISO 62, 50% RH |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ISO 62 |
| Water Vapor Transmission | 15.0 g/m²/day @Thickness 0.100 mm |
0.966 g/100 in²/day @Thickness 0.00394 in |
85% RH, film; ISO 15106-1 |
| Oxygen Transmission | 65.0 cc-mm/m²-24hr-atm @Thickness 0.100 mm |
165 cc-mil/100 in²-24hr-atm @Thickness 0.00394 in |
650 cc/m²-24hr-bar; film; b.o. ISO 2556 |
| 70.0 cc-mm/m²-24hr-atm @Thickness 0.0254 mm |
178 cc-mil/100 in²-24hr-atm @Thickness 0.00100 in |
2760 cc/m²-24hr-bar; film; b.o. ISO 2556 | |
| Nitrogen Transmission | 12.0 cc-mm/m²-24hr-atm @Thickness 0.100 mm |
30.5 cc-mil/100 in²-24hr-atm @Thickness 0.00394 in |
120 cc/m²-24hr-bar; film; b.o. ISO 2556 |
| 13.0 cc-mm/m²-24hr-atm @Thickness 0.0254 mm |
33.0 cc-mil/100 in²-24hr-atm @Thickness 0.00100 in |
510 cc/m²-24hr-bar; film; b.o. ISO 2556 | |
| Carbon Dioxide Transmission | 380 cc-mm/m²-24hr-atm @Thickness 0.100 mm |
965 cc-mil/100 in²-24hr-atm @Thickness 0.00394 in |
3800 cc/m²-24hr-bar; film; b.o. ISO 2556 |
| 429 cc-mm/m²-24hr-atm @Thickness 0.0254 mm |
1090 cc-mil/100 in²-24hr-atm @Thickness 0.00100 in |
16900 cc/m²-24hr-bar; film; b.o. ISO 2556 | |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 2.00 mm |
0.0070 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm @Thickness 2.00 mm |
0.0075 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
| Melt Flow | 6.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Puncture Resistance | 5600 N @Temperature 23.0 °C |
1260 lb (f) @Temperature 73.4 °F |
ISO 6603-2 |
| 6500 N @Temperature -30.0 °C |
1460 lb (f) @Temperature -22.0 °F |
ISO 6603-2 | |
| Ball Indentation Hardness | 116 MPa | 16800 psi | ISO 2039-1 |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | >= 50 % | >= 50 % | Nominal, 50 mm/min; ISO 527-1,-2 |
| 120 % | 120 % | 50 mm/min; b.o. ISO 527-1,-2 | |
| Elongation at Yield | 6.1 % | 6.1 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 74.0 MPa @Strain 3.50 % |
10700 psi @Strain 3.50 % |
2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Thickness 3.20 mm, Temperature -30.0 °C |
5.71 ft-lb/in² @Thickness 0.126 in, Temperature -22.0 °F |
complete break; b.o. ISO 180-A |
| 90.0 kJ/m² @Thickness 3.20 mm, Temperature 23.0 °C |
42.8 ft-lb/in² @Thickness 0.126 in, Temperature 73.4 °F |
partial break; b.o. ISO 180-A | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179-1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179-1eU | |
| NB @Temperature -60.0 °C |
NB @Temperature -76.0 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | 1.40 J/cm² @Thickness 3.00 mm, Temperature -30.0 °C |
6.66 ft-lb/in² @Thickness 0.118 in, Temperature -22.0 °F |
complete break; ISO 7391/b.o. ISO 179-1eA |
| 8.00 J/cm² @Thickness 3.00 mm, Temperature 23.0 °C |
38.1 ft-lb/in² @Thickness 0.118 in, Temperature 73.4 °F |
partial break; ISO 7391/b.o. ISO 179-1eA | |
| Puncture Energy | 60.0 J @Temperature 23.0 °C |
44.3 ft-lb @Temperature 73.4 °F |
ISO 6603-2 |
| 70.0 J @Temperature -30.0 °C |
51.6 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 65.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | cross-flow; ISO 8302 |
| Hot Ball Pressure Test | 137 °C | 279 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | ISO 75-1,-2 |
| Vicat Softening Point | 144 °C @Load 5.10 kg |
291 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 147 °C @Load 5.10 kg |
297 °F @Load 11.2 lb |
120°C/h; ISO 306 | |
| Glass Transition Temp, Tg | 145 °C | 293 °F | 10°C/min; ISO 11357-1,-2 |
| UL RTI, Electrical | 125 °C | 257 °F | UL 746B |
| UL RTI, Mechanical with Impact | 115 °C | 239 °F | UL 746B |
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
||
| Flash Point | 480 °C | 896 °F | ASTM D 1929 |
| 550 °C | 1020 °F | self ignition; ASTM D 1929 | |
| Oxygen Index | 27 % | 27 % | Method A; ISO 4589-2 |
| Glow Wire Test | 850 °C @Thickness 1.50 mm |
1560 °F @Thickness 0.0591 in |
b.o. EDF HN60 E.02 |
| 850 °C @Thickness 3.00 mm |
1560 °F @Thickness 0.118 in |
b.o. EDF HN60 E.02 | |
| 875 °C @Thickness 0.750 mm |
1610 °F @Thickness 0.0295 in |
GWFI; IEC 60695-2-12 | |
| 875 °C @Thickness 1.50 mm |
1610 °F @Thickness 0.0591 in |
GWFI; IEC 60695-2-12 | |
| 875 °C @Thickness 0.750 mm |
1610 °F @Thickness 0.0295 in |
GWIT; IEC 60695-2-13 | |
| 875 °C @Thickness 1.50 mm |
1610 °F @Thickness 0.0591 in |
GWIT; IEC 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 34.0 kV/mm @Thickness 1.00 mm |
864 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.00050 @Frequency 100 Hz |
0.00050 @Frequency 100 Hz |
IEC 60250 |
| 0.0095 @Frequency 1.00e+6 Hz |
0.0095 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 125 V | 125 V | CTI M; Solution B; IEC 60112 |
| 250 V | 250 V | Solution A; IEC 60112 |
Users viewing this material also viewed the following:
- Nitriflex NP-1021 Powdered Nitrile
- Parker Chomerics WIN-SHIELD™ F Conductive Film
- Ferro IX 2683 Passivation Glasses - High Voltage (Zn-B-Silicates)
- Dow Corning SILASTIC® LS 4-9040 FLUOROSILICONE RUBBER
- Eastman Tenite 350A0096914 Propionate Natural
- EMS-Grivory Grivory® XE 4116 nat PA1010-GF55
- Chosun Refractories PT-140 Plastic Refractory
- Axiall 8863 Moldings & Extrusions Flexible PVC
- DuPont Performance Polymers Zytel® FE5382 BK276 Nylon 612 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved