Covestro Makrolon® 1095 Polycarbonate, 15% Glass Filled

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled
Manufacturer	Covestro
Trade Name	Makrolon®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Covestro Makrolon® 1095 Polycarbonate, 15% Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

ISO 7391-PC,MR,(,,)-09-9,GF15Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 min15 % Glass fiber reinforcedHigh viscosityEasy releaseInjection molding - Melt temperature 310 - 330 °CExtrusionAvailable in opaque colors onlyHousings for power toolsPreprocessingMax. Water content

Physical Properties	Metric	English	Comments
Density	1.29 g/cc	0.0466 lb/in³	ISO 1183
	1.10 g/cc @Temperature 300 °C	0.0397 lb/in³ @Temperature 572 °F	Melt
Water Absorption	0.24 %	0.24 %	Similar to ISO 62
Moisture Absorption at Equilibrium	0.10 %	0.10 %	Similar to ISO 62
Linear Mold Shrinkage, Flow	0.0050 cm/cm	0.0050 in/in	ISO 294-4,2577
Linear Mold Shrinkage, Transverse	0.0050 cm/cm	0.0050 in/in	ISO 294-4,2577
Melt Flow	6.6 g/10 min @Load 1.20 kg, Temperature 300 °C	6.6 g/10 min @Load 2.65 lb, Temperature 572 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	45.0 MPa	6530 psi	ISO 527-1/-2
Elongation at Break	12 %	12 %	ISO 527-1/-2
Tensile Modulus	4.60 GPa	667 ksi	ISO 527-1/-2
Impact	3600	3600	Puncture - maximum force (N); ISO 6603-2
	2700 @Temperature -30.0 °C	2700 @Temperature -22.0 °F	Puncture - maximum force (N); ISO 6603-2
Puncture Energy	20.0 J	14.8 ft-lb	ISO 6603-2
	10.0 J @Temperature -30.0 °C	7.38 ft-lb @Temperature -22.0 °F	ISO 6603-2

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	35.0 µm/m-°C	19.4 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	65.0 µm/m-°C	36.1 µin/in-°F	ISO 11359-1/-2
Specific Heat Capacity	1.55 J/g-°C	0.370 BTU/lb-°F	Melt
Thermal Conductivity	0.198 W/m-K	1.37 BTU-in/hr-ft²-°F	Melt
Deflection Temperature at 0.46 MPa (66 psi)	142 °C	288 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	136 °C	277 °F	ISO 75-1/-2
Vicat Softening Point	144 °C	291 °F	50°C/h 50N; ISO 306
Flammability, UL94	V-2 @Thickness 1.50 mm	V-2 @Thickness 0.0591 in	IEC 60695-11-10
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	IEC 60695-11-10
Oxygen Index	27 %	27 %	ISO 4589-1/-2

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	IEC 60093
Dielectric Constant	3.2 @Frequency 100 Hz	3.2 @Frequency 100 Hz	IEC 60250
	3.2 @Frequency 1.00e+6 Hz	3.2 @Frequency 1.00e+6 Hz	IEC 60250
Dielectric Strength	36.0 kV/mm	914 kV/in	IEC 60243-1
Dissipation Factor	0.0010 @Frequency 100 Hz	0.0010 @Frequency 100 Hz	IEC 60250
	0.0090 @Frequency 1.00e+6 Hz	0.0090 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	175 V	175 V	IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	300 °C	572 °F	Injection Molding; ISO 294
	310 - 330 °C	590 - 626 °F
Mold Temperature	80.0 - 130 °C	176 - 266 °F
	110 °C	230 °F	Injection Molding; ISO 10724
Ejection Temperature	140 °C	284 °F
Injection Velocity	200 mm/sec	7.87 in/sec	ISO 294

Descriptive Properties	Value	Comments
Availability	Asia Pacific
	Europe
	India
	Near East/Africa
	North America
	South and Central America
Eff. thermal diffusivity (m²/s)	1.17E-07
Feature	Release agent
Form	Pellets
Process	Injection Molding
	Other Extrusion