- Fiberfil® J-61/20/E Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled
Fiberfil® J-61/20/E Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® J-61/20/E Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Water Absorption | 0.020 % | 0.020 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.0030 - 0.0040 cm/cm @Thickness 6.35 mm |
0.0030 - 0.0040 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 48.3 MPa | 7000 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 3.24 GPa | 470 ksi | ASTM D638 |
| Flexural Strength | 65.5 MPa | 9500 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm |
1.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs GD1000 Gd2(SO4)3·xH2O Gadolinium sulfate octahydrate
- LG Chemical LUMID GP2339B(W) PA66+GF33%, General Purpose
- H.C. Starck 2603 Molybdenum Powder Metallurgy Alloy ODS Mo-La
- Solvay Specialty Polymers Halar® 6012F Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- Solvay TECHNYL® A 218 V20 Black 21N PA66, 20% glass fiber, DRY
- Epoxy Technology EPO-TEK® OE101 Two Component Epoxy
- Braskem Idealis 500 Compression Molding High Molecular Weight Polyethylene
- Lanxess Durethan® BM 25 FN20 DUS013 000000 Nylon 6, 25% Mineral
- Phillips 66 COPYLENE® CM090L Polypropylene, High Impact Copolymer
Copyright © lookpolymers.com All Rights Reserved