Covestro Bayblend® FR 90 Polycarbonate + ABS Blend, Flame-Retardant  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® FR 90 Polycarbonate + ABS Blend, Flame-Retardant  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This product was discontinued prior to the separation.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Spiral Flow 71.0 cm

@Thickness 2.50 mm
28.0 in

@Thickness 0.0984 in
at 254°C melt temp.
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength, Ultimate 45.0 MPa
6530 psi
ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
ASTM D638
Elongation at Break 70 %
70 %
ASTM D638
Elongation at Yield 4.0 %
4.0 %
ASTM D638
Tensile Modulus 2.80 GPa
406 ksi
ASTM D638
Flexural Yield Strength 100 MPa
14500 psi
at 5% strain; ASTM D790
Flexural Modulus 2.80 GPa
406 ksi
ASTM D790
Izod Impact, Notched 5.30 J/cm

@Thickness 3.17 mm
9.93 ft-lb/in

@Thickness 0.125 in
ASTM D256
Impact Test 57.0 J

@Thickness 3.20 mm
42.0 ft-lb

@Thickness 0.126 in
Instrumented Total Impact; 3.2 mm thick, 12.5 mm dart, 75 mm clamp, 6.7 m/s; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear 77.0 µm/m-°C

@Temperature 20.0 °C
42.8 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 82.0 °C

@Thickness 6.35 mm
180 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Vicat Softening Point 91.0 °C
196 °F
Rate B/120; ASTM D1525
UL RTI, Electrical 85.0 °C

@Thickness 1.57 mm
185 °F

@Thickness 0.0618 in
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 1.57 mm
167 °F

@Thickness 0.0618 in
UL RTI, Mechanical without Impact 80.0 °C

@Thickness 1.57 mm
176 °F

@Thickness 0.0618 in
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Oxygen Index 30 %
30 %
ASTM D2836
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 112
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 93
Dielectric Constant 2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
ASTM D150
3.0

@Frequency 100 Hz
3.0

@Frequency 100 Hz
IEC 250
Dielectric Strength 29.9 kV/mm
759 kV/in
IEC 243
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
IEC 250
0.0070

@Frequency 1e+6 Hz
0.0070

@Frequency 1e+6 Hz
ASTM D150
Arc Resistance 60 - 120 sec

@Thickness 3.00 mm
60 - 120 sec

@Thickness 0.118 in
UL Rating PLC 6 (60-120 sec)
Comparative Tracking Index 300 V
300 V
IEC 112
Hot Wire Ignition, HWI 60 - 120 sec

@Thickness 3.00 mm
60 - 120 sec

@Thickness 0.118 in
UL Rating PLC 1 (60-120 sec)
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
UL Rating PLC 0 (>120 arcs)
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min

@Thickness 3.00 mm
>= 5.91 in/min

@Thickness 0.118 in
UL Rating PLC 4 (>150 mm/min.)
Processing Properties Metric English Comments
Melt Temperature 220 - 270 °C