- Cossa Polimeri ESTAPROP H 0360 T8 Polypropylene, 30% Mineral Filled
Cossa Polimeri ESTAPROP H 0360 T8 Polypropylene, 30% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Extrusion Grade , Polypropylene, Mineral Reinforced |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTAPROP H 0360 T8 Polypropylene, 30% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PP homopolymer 30% mineral fillerExtrusion gradeInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | ASTM D 955 |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ASTM D 638 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D 638 |
| Elongation at Break | 30 % | 30 % | ASTM D 638 |
| Tensile Modulus | 3.60 GPa | 522 ksi | ASTM D 638 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.150 J/cm @Temperature -20.0 °C |
0.281 ft-lb/in @Temperature -4.00 °F |
ASTM D 638 |
| 0.250 J/cm @Temperature 0.000 °C |
0.468 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 | |
| 0.350 J/cm @Temperature 23.0 °C |
0.656 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | 120°C/hr; ASTM D 648 |
| Vicat Softening Point | 95.0 °C @Load 5.00 kg |
203 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPH4504H PPC (Europe-Africa-Middle East)
- Gouda Vuurvast GOLITE 130 GM Refractory Insulating Castable
- Kaiser 4026 T651 Rod & Bar
- Polyram PlusTek PB840 Nylon 6, Impact Modified
- DuPont Performance Polymers Delrin® 100T BK602 Acetal (POM) (Unverified Data**)
- Domo 1101P Polypropylene Homopolymer
- Arlon 920-20Bxx-P0 0.020" (0.508 mm) Self-Fusing Silicone Tape
- Solvay RHODAPON® TL-40/A Surfactant
- Huntsman PE8010 Specialty Polyethylene (discontinued **)
- Polymer Resources PPX-FR3 Modified PPO, UL 94 V-1 with HDT of 265 F (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved