SABIC Innovative Plastics LNP LUBRICOMP QFL17RS PA 6/10
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP QFL17RS PA 6/10.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* QFL17RS is a compound based on Nylon 6/10 resin containing 35% Glass Fiber, 5% PTFE. Added features of this material include: Easy Release, Heat Stabilized, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.180 % | 0.180 % | 50% RH, 24 hrs; ASTM D570 |
| 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0015 cm/cm @Time 86400 sec |
0.0015 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0073 cm/cm @Time 86400 sec |
0.0073 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 183 MPa | 26500 psi | ISO 527 |
| 192 MPa | 27800 psi | ASTM D638 | |
| Elongation at Break | 3.4 % | 3.4 % | ISO 527 |
| 3.5 % | 3.5 % | ASTM D638 | |
| Tensile Modulus | 10.6 GPa | 1540 ksi | 1 mm/min; ISO 527 |
| 11.92 GPa | 1729 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 273 MPa | 39600 psi | ISO 178 |
| 282 MPa | 40900 psi | ASTM D790 | |
| Flexural Modulus | 9.03 GPa | 1310 ksi | ASTM D790 |
| 9.80 GPa | 1420 ksi | ISO 178 | |
| Izod Impact, Notched | 1.76 J/cm | 3.30 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.72 J/cm | 25.70 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 88.0 kJ/m² | 41.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 43.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 44.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 59.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 59.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C @Thickness 3.20 mm |
432 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Radici Radilon® A RV200 (dry) Nylon 66
- Flint Hills P4G4Z-011 Homopolymer Polypropylene
- Momentive Performance Materials Addisilâ„¢ 2060 E Industrial Extrusion Heat Cured Rubber
- Techmer ES HiFill® PA4/6 GF33 TL15 33% Glass Filled
- Wellman Wellamid® GF13-66 XE-N 13% Glass Fiber Reinforced Nylon 66, Lubricated & Heat Stabilized
- Lubrizol Estane® 2355-55DE Thermoplastic Polyurethane
- Eurofoam Porocell POR 303/B GR CR-Neoprene/NBR Foam
- Aremco Aremco-Seal™ 613 High Temperature Specialty Coatings Glass
- ChevronTexaco Regal® 320
Copyright © lookpolymers.com All Rights Reserved