Cosmic Plastics K61 Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Long Glass Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Cosmic Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cosmic Plastics K61 Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | |
| Apparent Bulk Density | 0.290 g/cc | 0.0105 lb/in³ | |
| Water Absorption | 0.25 % | 0.25 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
| Flexural Strength | 103 MPa | 14900 psi | |
| Compressive Strength | 186 MPa | 27000 psi | |
| Izod Impact, Notched | 2.40 J/cm | 4.50 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 24.0 µm/m-°C @Temperature 20.0 °C |
13.3 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Heat Distortion temperature |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | |
| Dielectric Constant | 3.9 @Frequency 1e+6 Hz |
3.9 @Frequency 1e+6 Hz |
Wet |
| 4.1 @Frequency 1000 Hz |
4.1 @Frequency 1000 Hz |
Wet | |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.0090 @Frequency 1000 Hz |
0.0090 @Frequency 1000 Hz |
Wet |
| 0.013 @Frequency 1e+6 Hz |
0.013 @Frequency 1e+6 Hz |
Wet | |
| Arc Resistance | 180 sec | 180 sec |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 165 °C | 275 - 329 °F | Molding temperature |
Users viewing this material also viewed the following:
- Lucite International Elvakon® 4470 High Gloss Acrylic Capstock
- Solvay Specialty Polymers Cogegum® AFR/765 Polyolefin
- A. Schulman POLYFORT™ FPP 1697HU High Flow Fortified Polypropylene
- Unitika elitel UE3300 Polyester, Flake
- A. Schulman POLYBATCH™ White LL8000 AP Concentrate Based In LLDPE
- Loctite® 3180 Deep Potting Polyurethane
- Trelleborg E647 EPDM Rubber
- Polimeri Europa Extir® LN 2000 Expandable Polystyrene
- ChevronTexaco Havoline® Prediluted 50/50 Anti-Freeze/Coolant
Copyright © lookpolymers.com All Rights Reserved