- Lotte Chemical Titan TITANLENE® LDF250YZ Low density polyethylene
Lotte Chemical Titan TITANLENE® LDF250YZ Low density polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Extrusion Grade |
| Manufacturer | Lotte Chemical Titan Holding Sdn. Bhd. (Former Titan Chemicals) |
| Trade Name | TITANLENE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lotte Chemical Titan TITANLENE® LDF250YZ Low density polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LDF250YZ is a low density polyethylene resin for film extrusion. LDF250YZ has no slip and anti-block additives. LDF250YZ meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 2.1 & (c) 2.2.Applications: Medium duty shrink film Shopper bags Form fill and seal packagingAdditives: BarefootAdvantages: Good mechanical properties and stiffnessInformation provided by Titan Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Base Resin Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 50.0 microns | 1.97 mil | extruded at 2.5:1 BUR |
| Base Resin Melt Index | 0.75 g/10 min | 0.75 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 370 % | 370 % | ASTM D882 |
| Film Elongation at Break, TD | 560 % | 560 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 7.00 g/micron | 178 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.00 g/micron | 102 g/mil | ASTM D1922 |
| Dart Drop | 4.00 g/micron | 102 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 27.5 MPa | 3990 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 24.5 MPa | 3550 psi | ASTM D882 |
| 1% Secant Modulus, MD | 215.74 MPa | 31291 psi | ASTM D882 |
| 1% Secant Modulus, TD | 235.36 MPa | 34136 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 93.0 °C | 199 °F | resin; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 160 - 190 °C | 320 - 374 °F | |
| Blow-up Ratio (BUR) | 1.5 - 3.0 | 1.5 - 3.0 |
Users viewing this material also viewed the following:
- Karina 813D02/28-IS Yellow PVC Compound
- SABIC Innovative Plastics LNP STAT-KON DD0009E PC
- A. Schulman FORMION™ FI 391E Ionomer
- A. Schulman INVISION™ VX-5070UI Soft Touch Polyolefin Thermoplastic
- Toyobo A3080A Thermoplastic Polyurethane Elastomer, Injection Grade
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Non-Black, Soft Clay
- DuPont Performance Polymers Kalrez® 6375 FFKM Perfluoroelastomer
- Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW
- EG60D-B20 Polyurethane-based Biomedical Elastomer
Copyright © lookpolymers.com All Rights Reserved