Cosmic Plastics ID-50 Dacron Filled Ortho Diallyl Phthalate Molding Compound
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP), Molded, Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Cosmic Plastics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cosmic Plastics ID-50 Dacron Filled Ortho Diallyl Phthalate Molding Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | |
| Apparent Bulk Density | 0.230 g/cc | 0.00831 lb/in³ | |
| Water Absorption | 0.35 % | 0.35 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 25.0 - 36.0 MPa | 3630 - 5220 psi | |
| Flexural Strength | 76.0 MPa | 11000 psi | |
| Compressive Strength | 141 MPa | 20500 psi | |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | Heat Distortion temperature |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz |
3.6 @Frequency 1e+6 Hz |
Wet |
| 3.8 @Frequency 1000 Hz |
3.8 @Frequency 1000 Hz |
Wet | |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.015 @Frequency 1000 Hz |
0.015 @Frequency 1000 Hz |
Wet |
| 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
Wet | |
| Arc Resistance | 115 sec | 115 sec |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 165 °C | 275 - 329 °F | Molding temperature |
Users viewing this material also viewed the following:
- Polimeri Europa Clearflex® FG B3 Very Low Density Polyethylene
- Ovation Polymers UTTAP QU BM513 GF BM Nylon, 13% Glass Reinforced
- SABIC Innovative Plastics Lexan® EXL1434T PC Copolymer (Europe-Africa-Middle East)
- Lehmann & Voss LUVOCOM® 50-7446 Polycarbonate, with carbon fiber, PTFE, lubricant modified
- H.C. Starck Grade B Titanium Carbonitride
- Multibase C6-265 VAROX DBPH Dow-Corning Class VI Elastomer
- SABIC Innovative Plastics LNP Stat-kon AD000Z ABS
- Teknor Apex Uniprene® UN-2420D Thermoplastic Vulcanizate
- Colorite Polymers 3876 General Purpose Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved