- Clariant Renol PCSP0009 Polycarbonate, 15% Glass Fiber, Silicone Lubricated
Clariant Renol PCSP0009 Polycarbonate, 15% Glass Fiber, Silicone Lubricated
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PCSP0009 Polycarbonate, 15% Glass Fiber, Silicone Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 96.5 MPa | 14000 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 274 - 316 °C | 525 - 600 °F | |
| Mold Temperature | 82.2 - 121 °C | 180 - 250 °F | |
| Dry Time | 2 - 4 hour @Temperature 121 °C |
2 - 4 hour @Temperature 250 °F |
to ensure the moisture level is less than 0.02% |
| Injection Pressure | 41.4 - 82.7 MPa | 6000 - 12000 psi | Secondary |
| 68.9 - 138 MPa | 10000 - 20000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Oceanchem Group Sodium Bromide (NaBr)
- Omni Plastics OmniLon™ 6 PA6 IM20 Unfilled/ Impact Modified Nylon
- Solvay Technyl® C216V25 25% Glass Filled Nylon 6
- SABIC Innovative Plastics LNP STAT-KON KX96321 POM
- Borealis BorSafe™ ME3420 MDPE Compound for Pressure Pipes
- Trelleborg Emerson & Cuming Eccobond® 45C Two-Component General Purpose Epoxy Adhesive
- Chosun Refractories FAM-1 Flame-Gunning Repair Refractory
- Cast Nylons Nycast® 6MPB Plasticized Nylon 6
- Arlon 30600R010 0.010" (0.254 mm) Uncured/Unsupported Silicone Rubber on a Release Carrier
Copyright © lookpolymers.com All Rights Reserved