SCG Chemicals EL-Proâ„¢ P750J Polypropylene Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Pro™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Proâ„¢ P750J Polypropylene Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:Excellent clarityHigh productivityGood processability and stiffnessHigh glossOdorlessSafe for food contactRecommended Applications:Food container, utensilMedical parts such as syringePremium articles with excellent clarityInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D1505 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Thickness 2.00 mm |
0.014 in/in @Thickness 0.0787 in |
TPE Method |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 2.00 mm |
0.014 in/in @Thickness 0.0787 in |
TPE Method |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D638 |
| Tensile Strength, Yield | 29.4 MPa | 4270 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Modulus | 1.18 GPa | 171 ksi | ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Temperature 0.000 °C |
0.735 ft-lb/in @Temperature 32.0 °F |
ASTM D256 |
| 0.686 J/cm @Temperature 23.0 °C |
1.29 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 150 °C | 302 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 |
| Vicat Softening Point | 130 °C | 266 °F | ASTM D1525 |
| Brittleness Temperature | -20.0 °C | -4.00 °F | ASTM D746 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 12 % @Thickness 1.00 mm |
12 % @Thickness 0.0394 in |
ASTM D1003 |
| Gloss | 77 % @Thickness 1.00 mm |
77 % @Thickness 0.0394 in |
ASTM D2457 |
Users viewing this material also viewed the following:
- RheTech Products G40P100-00 40% Glass Fiber Reinforced Polypropylene, Natural
- Premix Thermoplastics PRE-ELEC® PS 1326
- Solvay TECHNYL® C 216 PA6, Conditioned
- Shinil Chemical SHINSTRA PBT SBV1015 Structural Polymer Lamp Housing
- Covestro Baygal® 90 IK 69 Polyurethane
- EMS-Grivory Grivory® TSZ 3 PA666
- DuPont Teijin Films Melinex® 339 Polyester Film, 700 Gauge
- Fainplast Compounds CL 80/1 Flexible PVC, Sheathing
- Dow Styrofoam™ Polystyrene Rigid Foam Insulation
- Braskem TI2900C High Crystallinity Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved