Chi Mei Polylac® PA-747F ABS - Extrusion
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-747F ABS - Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Refrigerator
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.30 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
3.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO-1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Ball Indentation Hardness | 99.0 MPa | 14400 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; ISO 527 |
| Flexural Strength | 66.0 MPa | 9570 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 2.66 J/cm @Thickness 6.35 mm |
4.98 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 3.32 J/cm @Thickness 3.17 mm |
6.22 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 2.70 J/cm² | 12.8 ft-lb/in² | ISO 179 |
| Impact | 17.0 | 17.0 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | unannealed; ISO 75 |
| 100 °C | 212 °F | annealed; ISO 75 | |
| Vicat Softening Point | 101 °C @Load 5.00 kg |
214 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 105 °C @Load 5.00 kg |
221 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 106 °C @Load 1.00 kg |
223 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 108 °C @Load 1.00 kg |
226 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Nylene® 401D, Nylon 6
- Quadrant EPP Nylatron® GSM Blue Nylon, Cast Oil & MoS2 Filled Type 6 (ASTM Product Data Sheet)
- Garlock BLUE-GARD® 3300 Compressed Aramid Fiber Gasketing, Neoprene Binder
- SGL Carbon Group PANOX® LB C076 SSC Oxidized Textile Fiber, Crimped staple fiber, For felts and non-wovens
- Total PS CPDS 855S Chlorine and Bromine Free Flame Retardant High Impact Polystyrene
- Azoty Tarnow™ Tarnamid® T-27 MK30 Polyamide 6 - Mineral Reinforced
- Alliance Polymers Viprene™ P90A-22U-BLK Thermoplastic Vulcanizate Elastomer
- Alliance A-6S Alnico Magnetic Material
- A. Schulman ComAlloy Comtuf® 164 Polypropylene, Mineral Reinforced, Chemically Coupled, Impact Modified
- LyondellBasell Hifax™ CA207A Thermoplastic Polyolefin Elastomer
Copyright © lookpolymers.com All Rights Reserved