Chevron Phillips Marlex® K203 LLDPE Sheet Extrusion

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Extrusion Grade
Manufacturer Chevron Phillips Chemical Company LP
Trade Name Marlex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips Marlex® K203 LLDPE Sheet Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resin Type: Hexene CopolymerCharacteristics: Outstanding ESCRBroad fusion rangeExcellent melt strengthGood processabilityExcellent flexibilityImproved output and texturingApplications: Coextruded cap layers for HDPEBlends with HDPELandfill covers and capsMasterbatch projectsRound and flat die projectsInformation provided by Chevron Phillips.
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
ASTM D1505
ESCR 100% Igepal® >= 1500 hour
>= 1500 hour
Condition C; ASTM D1693
ESCR 10% Igepal® >= 1500 hour
>= 1500 hour
Condition B; ASTM D1693
Melt Flow 15 g/10 min
15 g/10 min
Condition 190/21.6, HLMI; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 55
55
ASTM D2240
Tensile Strength, Yield 12.0 MPa
1740 psi
2 in/min, Type IV bar; ASTM D638
Elongation at Break 750 %
750 %
2 in/min, Type IV bar; ASTM D638
Flexural Modulus 0.480 GPa
69.6 ksi
Tangent, 16:1 span:depth,0.5in/min; ASTM D790
Tensile Impact Strength 800 kJ/m²
381 ft-lb/in²
Type S bar; ASTM D1822
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 51.0 °C
124 °F
Method A; ASTM D648
Vicat Softening Point 104 °C
219 °F
Loading 1, Rate A; ASTM D1525
Brittleness Temperature <= -75.0 °C
<= -103 °F
Type A clamp, type 1 specimen; ASTM D746
Descriptive Properties Value Comments
SP-NCTL Min 1000
Single-point notched constant tensile load