Dow Nordel® IP 4520 Molded Brake Part
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Dow Chemical |
| Trade Name | Nordel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Nordel® IP 4520 Molded Brake Part.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationNordel® IP 4520
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.116 g/cc | 0.04032 lb/in³ | |
| Mooney Viscosity | 82 @Temperature 100 °C |
82 @Temperature 212 °F |
ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 18.8 MPa | 2730 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 155 % | 155 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 50% Modulus | 0.00380 GPa | 0.551 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.0104 GPa | 1.51 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 17.0 kN/m | 97.0 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 7.0 % @Temperature 125 °C |
7.0 % @Temperature 257 °F |
Pellets cured MDR TC95 + 15 min at 160°C, 70 hr at 125°C; Method B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -43.0 °C | -45.4 °F | Temperature Retraction, TR-10 |
Users viewing this material also viewed the following:
- MV Labs MN200 MnBr2·4H2O Manganese(II) bromide tetrahydrate
- Solvay Specialty Polymers Ixef® 1023 Polyarylamide (PARA) (discontinued **)
- Stellarchem GP-860HD TPE Compound
- Teknor Apex Telcar® TL EF-6123 Thermoplastic Elastomer
- TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Fastener Stock
- Dow Corning 2-8035 CATIONIC EMULSION
- Addiplast Addilene J 520 M20 Polypropylene Copolymer
- Arkema Group Orgalloy® LE 60ES Flexible Nylon Alloy (Conditioned)
- Hexion Bakelite™ PF 4260 Phenolic Formaldehyde Resin, Resistant to High Temperatures, Improved Electrical Properties, Low Shrinkage, High Mechanical Strength
Copyright © lookpolymers.com All Rights Reserved