Chevron Phillips 7109CLT LLDPE Blown Film Resin, Hexene Copolymer  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips 7109CLT LLDPE Blown Film Resin, Hexene Copolymer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resin Type: Hexene Copolymer, High Slip, Very High Antiblock Version of 7109T, Cast/Blown Film ResinCharacteristics: Good Stiffness at Thin Gauges, Good Drawdown, Can be used straight or blended with LDPE or HDPE. Slip 2000 ppm. Antiblock 7500 ppm.Applications:Industrial Liners, Garment Bags, Carrier Bags, CoextrusionsProcessing Conditions: Extruder 6.35 cm. Screw L/D Ratio 24:1. Die Opening 0.1905 cm. Blow-Up Ratio 2:1.Film properties below based on film thickness of 31.8 µm.Data provided by Chevron Chemical.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D1505
Melt Flow 0.90 g/10 min
0.90 g/10 min
Condition E; ASTM D 1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 440 %
440 %
ASTM D882
Film Elongation at Break, TD 580 %
580 %
ASTM D882
Secant Modulus, MD 0.260 GPa
37.7 ksi
ASTM D882
Secant Modulus, TD 0.310 GPa
45.0 ksi
ASTM D882
Coefficient of Friction 0.13
0.13
ASTM D1894
Elmendorf Tear Strength, MD 15.7 g/micron
400 g/mil
Notched; ASTM D1922
Elmendorf Tear Strength, TD 35.8 g/micron
910 g/mil
ASTM D1922
Dart Drop 4.10 g/micron
104 g/mil
F<sub>50</sub>; 1.5 in. dart/26 in. drop height; ASTM D 1709
Film Tensile Strength at Break, MD 30.0 MPa
4350 psi
ASTM D882
Film Tensile Strength at Break, TD 30.0 MPa
4350 psi
ASTM D882
Optical Properties Metric English Comments
Haze 13 %
13 %
ASTM D2457
Gloss 52 %
52 %
at 45°. ASTM D 2457
95 %
95 %
at 60°. ASTM D 2457
Processing Properties Metric English Comments
Melt Temperature 220 °C
428 °F