- Chase Plastics CP Pryme® NN133TL (Dry) Nylon 66, 33% Glass Fiber Reinforced, Lubricated, Impact Modified
Chase Plastics CP Pryme® NN133TL (Dry) Nylon 66, 33% Glass Fiber Reinforced, Lubricated, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® NN133TL (Dry) Nylon 66, 33% Glass Fiber Reinforced, Lubricated, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Impact modifiedLubricatedGood toughnessForm: PelletsInformation provided by Chase Plastics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Filler Content | 33 % | 33 % | |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 141 MPa | 20500 psi | ASTM D638 |
| Elongation at Break | 4.5 % | 4.5 % | ASTM D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| Flexural Modulus | 7.31 GPa | 1060 ksi | ASTM D790 |
| Izod Impact, Notched | 2.08 J/cm | 3.90 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 °C | 491 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Dutral® TER 9046 Ethylene - Propylene - Diene Terpolymer
- Overview of materials for Acetal Copolymer, Unreinforced
- Kazanorgsintez 108-274 Thermostabilized Low Density Polyethylene Composition for Radiation Modification
- Fiberfil® J-69/10/E/UV High performance polypropylene Homopolymer, 10% Glass Reinforced, Chemically coupled, UV Stabilized
- Lucent Polymers GPCB-110 Polycarbonate+PBT, 10% Glass Fiber Reinforced
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with Plasthall DOZ
- Toyobo A3080A Thermoplastic Polyurethane Elastomer, Injection Grade
- EPICHEM PA 6/66 GF 30 Polyamide 6/66, 30% Glass
- Eurostar Staramide PF006 PA6, 30% Glass Fiber Filled, Injection Molded
- Aclo Accutech Polypropylene Copolymer CP0437C40L Calcium Reinforced
Copyright © lookpolymers.com All Rights Reserved