Chase Plastics CP Pryme® NN100L (DAM) Nylon 66, Internally Lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® NN100L (DAM) Nylon 66, Internally Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chase Plastics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Silikony Polskie Polsil OM 2000 Methyl Silicone Fluid
- Styrolution Terblend® N NG-06 30% Glass Filled ABS/PA6 (Dry)
- Styron LGF 9621 Homopolymer Polypropylene
- Sax Polymers SAXAMID 236F4Q32 Nylon 6.6, 20% Glass Fiber
- A. Schulman POLYBATCH™ Beige 6027E Concentrate Based In Polyethylene
- A. Schulman POLYBATCH™ FTA-50-P Concentrate Based In LLDPE
- Dow Corning 193C Fluid
- Dow INSPIRE™ D500.00 Developmental Performance Polymer
- Aaron Industries AAROPRENE® GFIPP 2040 High Impact Glass Filled Polypropylene
- Akro-Plastic Akromid® A3 4 S1 PA, Cold-Impact Resistant (discontinued **)
Copyright © lookpolymers.com All Rights Reserved