- Carpenter HyMu "80"® Electronic Alloy, Cold Drawn Bar
Carpenter HyMu "80"® Electronic Alloy, Cold Drawn Bar
| Category | Metal , Electronic/Magnetic Alloy , Nonferrous Metal , Nickel Alloy |
| Manufacturer | Carpenter Technology Corporation (Cartech) |
| Trade Name | HyMu "80"® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Carpenter HyMu "80"® Electronic Alloy, Cold Drawn Bar.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Carpenter Technology Corporation.Carpenter HyMu “80” ® alloy is an unoriented, 80% nickel-iron-molybdenum alloy which offers extremely high initial permeability as well as maximum permeability with minimum hysteresis loss.Carpenter HyMu “80” alloy has been used primarily in transformer cores, tape wound toroids and laminations where compactness and weight factors are important. It has also been used for shielding to protect electrical components from stray magnetic fields.HyMu "80"® is a registered trademark of Carpenter Technology Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.74 g/cc | 0.316 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell B | 97 | 97 | |
| Tensile Strength, Ultimate | 669 MPa | 97000 psi | |
| Tensile Strength, Yield | 414 MPa | 60000 psi | Offset not specified |
| Elongation at Break | 37 % | 37 % | |
| Reduction of Area | 71 % | 71 % | |
| Modulus of Elasticity | 232 GPa | 33600 ksi | |
| Izod Impact | 163 J | 120 ft-lb |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.0 µm/m-°C @Temperature 25.0 - 300 °C |
6.67 µin/in-°F @Temperature 77.0 - 572 °F |
|
| 12.3 µm/m-°C @Temperature 25.0 - 50.0 °C |
6.83 µin/in-°F @Temperature 77.0 - 122 °F |
||
| Specific Heat Capacity | 0.494 J/g-°C | 0.118 BTU/lb-°F | |
| Thermal Conductivity | 34.6 W/m-K | 240 BTU-in/hr-ft²-°F | |
| Melting Point | 1454 °C | 2649 °F | |
| Solidus | 1454 °C | 2649 °F | Melting Point |
| Liquidus | 1454 °C | 2649 °F | Melting Point |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.020 % | 0.020 % | |
| Iron, Fe | 15 % | 15 % | as remainder |
| Manganese, Mn | 0.50 % | 0.50 % | |
| Molybdenum, Mo | 4.2 % | 4.2 % | |
| Nickel, Ni | 80 % | 80 % | |
| Silicon, Si | 0.35 % | 0.35 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000580 ohm-cm | 0.0000580 ohm-cm | Temp Coefficient 0.0011/ºC (-17.8-449ºC) |
| Curie Temperature | 460 °C | 860 °F |
Users viewing this material also viewed the following:
- Radici Radilon® S 32HS (cond.) Nylon 6
- 3M Scotch-Weld™ 3549 B/A Brown Two-Part Urethane Adhesive 3549 B/A Brown (discontinued **)
- Lehmann & Voss LUVOCOM® 19-8263 Polyamide 46, with carbon fiber and glass fiber, lubricant modified
- Fibre Glast 573 Style 120 E-Glass Fiberglass Fabric
- DuPont Surlyn® SG201U NC010 Supergloss Molding Alloy
- Chosun Refractories CSN-A116 Plate Brick
- Buckeye Polymers BP FLEX D5618 T RXF Thermoplastic Polyolefin
- Plaslok 5314 Black (COM) Impact Grade Phenolic Molding Compound (discontinued **)
- Cosmic Plastics 224 Dacron Filled Ortho Diallyl Phthalate Molding Compound
Copyright © lookpolymers.com All Rights Reserved