- PolyOne Geon™ L6105 natural Polyvinyl Chloride, Rigid (PVC, Rigid)
PolyOne Geon™ L6105 natural Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ L6105 natural Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 81 | 81 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 54.8 MPa | 7950 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 4.72 GPa | 685 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 95.1 MPa | 13800 psi | ASTM D790 |
| Flexural Modulus | 4.54 GPa | 658 ksi | ASTM D790 |
| Izod Impact, Notched | 0.430 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.806 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded; ASTM D256A |
| Dart Drop Total Energy | 53.4 J/cm @Temperature 23.0 °C |
0.100 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 53.4 J/cm @Temperature 23.0 °C |
0.100 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.0 µm/m-°C | 25.6 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 78.9 °C @Treatment Temp. 60.0 °C |
174 °F @Treatment Temp. 140 °F |
Annealed; ASTM D648 |
| 77.2 °C @Treatment Temp. 50.0 °C, Thickness 3.18 mm |
171 °F @Treatment Temp. 122 °F, Thickness 0.125 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C @Treatment Temp. 60.0 °C |
171 °F @Treatment Temp. 140 °F |
Annealed; ASTM D648 |
| 73.9 °C @Treatment Temp. 50.0 °C, Thickness 3.18 mm |
165 °F @Treatment Temp. 122 °F, Thickness 0.125 in |
Annealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 - 3.00 mm |
V-0 @Thickness 0.0591 - 0.118 in |
natural; UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | High Stiffness | |
| Low CLTE | ||
| Forms | Cube | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 12474 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | General Purpose | |
| Profiles |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 21-7979 Polyamide 6/6T, with glass fiber, 8-mm-granulate
- Kotec Carbotex KG-30F15 Polycarbonate, Wear Resistant, 30% Glass Fiber Reinforced
- Schwartz Technical Plastics LAMIGAMID® 309 Cast Polyamide 6, Oil Filled, Dry
- A. Schulman POLYBATCH™ White B8750A Concentrate Based In HDPE
- Unipetrol PE HD LITEN® BB 85 HDPE
- Wellman Wellamid® GFX1624-BK(PTFE) 30% Glass Fiber Reinforced, Lubricated Nylon 66
- Domo 2448L Polypropylene Copolymer
- BASF Ultramid® B3ZG8 BK 20560 40% Glass Filled PA6-1 (Dry)
- Alliance BIS-82 Bonded (Composite) Magnetic Material
- 3M Scotch-Weld™ DP100 FR Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved