Lubrizol Advanced Materials Pearlthane® ECO D12T85 Thermoplastic Polyurethane
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | Lubrizol Advanced Materials Manufacturing S. S.L. (Former Merquinsa) |
| Trade Name | Pearlthane® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Advanced Materials Pearlthane® ECO D12T85 Thermoplastic Polyurethane.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Pearlthane® ECO D12T85 is a 85 Shore A, High Performance natural TPU based on Renewable Sources with ca. 46% renewable content according to ASTM D6866 for Injection Moulding applications. This natural TPU resin features properties similar to standard TPU of same hardness (i.e. excellent mechanical
properties and abrasion resistance).Pearlthane® ECO D12T85 enhances the performance of a wide range of end use products that ranges from
automotive, consumer electronics and sport and leisure applications among others where environmentally friendly materials can bring value to the end product.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D-792 |
| Moisture Absorption at Equilibrium | <= 0.10 % | <= 0.10 % | MQSA 44 |
| Melt Flow | 10 g/10 min @Load 21.6 kg, Temperature 175 - 185 °C |
10 g/10 min @Load 47.6 lb, Temperature 347 - 365 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 85 | 85 | ASTM D-2240 |
| Tensile Strength | 35.00 MPa | 5076 psi | ASTM D-412 |
| Tensile Strength, Yield | 5.998 MPa @Strain 100 % |
870.0 psi @Strain 100 % |
ASTM D-412 |
| 22.00 MPa @Strain 300 % |
3191 psi @Strain 300 % |
ASTM D-412 | |
| Elongation at Break | 400 % | 400 % | ASTM D-412 |
| Abrasion | 20 | 20 | mm<sup>3</sup> Loss; DIN 53.516 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 190 - 200 °C | 374 - 392 °F | Temperature range at which MFI = 10 g/10 min at 21.6 kg.; MQSA 111 |
| Glass Transition Temp, Tg | -38.9 °C | -38.0 °F | DSC, 50°F/10min; DIN 51.007 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 195 °C | 383 °F | |
| Nozzle Temperature | 210 °C | 410 °F | |
| Mold Temperature | 35.0 °C | 95.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Biobased Content (%) | 44 | ASTM D-6866 |
| Compression Zone Temperature | 385°F | |
| Metering Zone Temperature | 390°F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics EXTEM UH1016 TPI Blend (Asia Pacific)
- Polymer Resources TP-G30 Polybutylene Terephthalate, 30% Glass Reinforced
- Momentive Performance Materials Siloprenâ„¢ LIM 8040 Liquid Silicone Rubber - Healthcare
- H.C. Starck F-21-5 Pure Molybdenum, Foil
- H.C. Starck Pure Molybdenum GME Glass Melting Electrodes
- Fiberfil® J-62/30/E8 Polypropylene Copolymer, 30% Glass Fiber Reinforced, Chemically coupled
- Sibur 23007-30T Superior Quality Polypropylene Copolymer
- A. Schulman INVISION™ VX-5065UI Soft Touch Polyolefin Thermoplastic
- Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (4 mm Molded Thickness)
- Techmer ES HiFill FR® PA6/6 GF15 FR BK 15% Glass Filled
Copyright © lookpolymers.com All Rights Reserved