Carpenter BioDur™ CCM® Medical Implant Alloy, Hot Worked

Category	Metal , Nonferrous Metal , Cobalt Alloy , Superalloy
Manufacturer	Carpenter Technology Corporation (Cartech)
Trade Name	BioDur™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Carpenter BioDur™ CCM® Medical Implant Alloy, Hot Worked.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur Carpenter CCM alloy is produced by vacuum induction melting (VIM) followed by electroslag remelting (ESR).BioDur™ and Carpenter CCM® are trademarks of Carpenter Technology Corporation.

Physical Properties	Metric	English	Comments
Density	8.287 g/cc	0.2994 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Brinell	311	311	Estimated from Rockwell C for Brinell test with 3000 kg load, 10 mm ball.
Hardness, Knoop	337	337	Estimated from Rockwell C
Hardness, Rockwell C	33	33
Hardness, Vickers	325	325	Estimated from Rockwell C
Tensile Strength, Ultimate	1100 MPa	160000 psi
Tensile Strength, Yield	760 MPa @Strain 0.200 %	110000 psi @Strain 0.200 %
Elongation at Break	25 %	25 %	in 4D
Reduction of Area	23 %	23 %

Thermal Properties	Metric	English
CTE, linear	13.18 µm/m-°C @Temperature 0.000 - 100 °C	7.322 µin/in-°F @Temperature 32.0 - 212 °F
	13.47 µm/m-°C @Temperature 25.0 - 300 °C	7.483 µin/in-°F @Temperature 77.0 - 572 °F
	15.09 µm/m-°C @Temperature 25.0 - 700 °C	8.383 µin/in-°F @Temperature 77.0 - 1290 °F
	17.08 µm/m-°C @Temperature 25.0 - 1150 °C	9.489 µin/in-°F @Temperature 77.0 - 2100 °F
Specific Heat Capacity	0.470 J/g-°C @Temperature 23.0 °C	0.112 BTU/lb-°F @Temperature 73.4 °F
	0.590 J/g-°C @Temperature 600 °C	0.141 BTU/lb-°F @Temperature 1110 °F
	0.673 J/g-°C @Temperature 1100 °C	0.161 BTU/lb-°F @Temperature 2010 °F
Thermal Conductivity	12.66 W/m-K @Temperature 23.0 °C	87.86 BTU-in/hr-ft²-°F @Temperature 73.4 °F
	25.76 W/m-K @Temperature 600 °C	178.8 BTU-in/hr-ft²-°F @Temperature 1110 °F
	35.57 W/m-K @Temperature 1177 °C	246.9 BTU-in/hr-ft²-°F @Temperature 2151 °F

Component Elements Properties	Metric	English	Comments
Carbon, C	<= 0.10 %	<= 0.10 %
Chromium, Cr	26 - 30 %	26 - 30 %
Cobalt, Co	62 %	62 %	as remainder
Iron, Fe	<= 0.75 %	<= 0.75 %
Manganese, Mn	<= 1.0 %	<= 1.0 %
Molybdenum, Mo	5.0 - 7.0 %	5.0 - 7.0 %
Nickel, Ni	<= 1.0 %	<= 1.0 %
Nitrogen, N	<= 0.25 %	<= 0.25 %
Silicon, Si	<= 1.0 %	<= 1.0 %