- Polymer Property : Tensile Strength, Yield = 110000 psi
Polymer Property : Tensile Strength, Yield = 110000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | >= 758 MPa @Strain 0.200 % |
>= 110000 psi @Strain 0.200 % |
|
| Materion ToughMet® T3 AT110 (OD≥4") ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have e.. |
|||
| Tensile Strength, Yield | >= 760 MPa | >= 110000 psi | |
| MetalTek IN® 718 UNS N07718 Centri-Vac Nickel Cobalt Based Alloy Information provided by MetalTek |
|||
| Tensile Strength, Yield | >= 760 MPa | >= 110000 psi | |
| MetalTek MTEK 718 Cast UNS N07718 Severe Corrosion and Heat Resistant Alloy Information provided by MetalTek |
|||
| Tensile Strength, Yield | 755 MPa | 110000 psi | |
| Haynes Hastelloy® W alloy, gas metal arc welds, aged 1000 hours at 650°C (1200°F) Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| Tensile Strength, Yield | 760 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
| Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Tensile Strength, Yield | 760 MPa @Strain 0.200 %, Temperature 95.0 °C |
110000 psi @Strain 0.200 %, Temperature 203 °F |
|
| Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Tensile Strength, Yield | 758 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
| Haynes Hastelloy® C-22® alloy, 10% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Tensile Strength, Yield | 758 MPa | 110000 psi | |
| HP Alloys Alloy 718, 10% Cold Worked 10% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
| Tensile Strength, Yield | 758 - 965 MPa @Strain 0.200 % |
110000 - 140000 psi @Strain 0.200 % |
|
| Special Metals DURANICKEL® 301 (UNS N03301) Annealed and Aged Rod and Bar Tensile strength (ultimate and yield), compressive strength, hardness, and elongation values reported here are typical for Annealed and Aged Rod and Bar specifically. Other property values are typic.. |
|||
| Tensile Strength, Yield | 758 MPa | 110000 psi | Cold Worked |
| Special Metals INCOLOY® alloy 028 Austenitic Stainless Steel INCOLOY® alloy 028 (UNS N08028/W. Nr. 1.4563) is a highly alloyed austenitic stainless steel offering resistance to a variety of corrosive media. By virtue of its contents of chromium and molybd.. |
|||
| Tensile Strength, Yield | 760 MPa @Strain 0.200 %, Temperature 550 °C |
110000 psi @Strain 0.200 %, Temperature 1020 °F |
Precipitation Hardened prior to test |
| Special Metals INCONEL® Alloy X-750 A nickel-chromium alloy similar to INCONEL alloy 600 but made precipitation hardenable by additions of aluminum and titanium. The alloy has good resistance to corrosion and oxidation along with hig.. |
|||
| Tensile Strength, Yield | 760 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
Precipitation Hardened |
| Special Metals NI-SPAN-C® Alloy 902 A nickel-iron-chromium alloy made precipitation hardenable by additions of aluminum and titanium. The titanium content also helps provide a controllable thermoelastic coefficient, which is the allo.. |
|||
| Tensile Strength, Yield | 758 - 896 MPa @Strain 0.200 % |
110000 - 130000 psi @Strain 0.200 % |
Heat Treatment (Condition T HRc 26-32) |
| Schmolz + Bickenbach 416 Stainless Steel Bar Description: Ugitech’s 416 is free machining martensitic grade. The unique production process—developed exclusively by Ugitech—results in a product that delivers superior productivity.. |
|||
| Tensile Strength, Yield | 758 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
| Schmolz + Bickenbach MoldMAX LH® Low Hard - Copper Alloy Description: Brush Wellman’s MoldMAX LH® (Low Hard) is a premium copper mold alloy that provides hardness and strength comparable with standard AISI P-20 tool steel and a thermal conductivit.. |
|||
| Tensile Strength, Yield | >= 759 MPa @Strain 0.200 % |
>= 110000 psi @Strain 0.200 % |
Longitudinal |
| TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; Medium To High Strength General-Purpose Alloy Minimum tensile property data below are specific to this MatWeb entry; other specific form/thickness entries are also available in MatWeb.Features: A .. |
|||
| Tensile Strength, Yield | >= 760 MPa @Strain 0.200 % |
>= 110000 psi @Strain 0.200 % |
L and LT Directions |
| TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; 1.75 - 2.50 in Rod or Thickness; Per ASTM F136) Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to this MatWeb entry; other specific form/thickness entries are also available in MatWeb.Features: A.. |
|||
| Tensile Strength, Yield | >= 759 MPa @Strain 0.200 % |
>= 110000 psi @Strain 0.200 % |
L and LT Directions |
| TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Solution Treated; 0.025 - 1.000 in Sheet and Plate; Per ASTM B265) Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to this MatWeb entry; other specific form/thickness entries are also available in MatWeb.Features: A.. |
|||
| Tensile Strength, Yield | >= 758 MPa | >= 110000 psi | 0.2% Offset |
| Eagle Brass 301 Austenitic Stainless Steel, 1/2 Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
| Tensile Strength, Yield | >= 758 MPa | >= 110000 psi | 0.2% Offset |
| Eagle Brass 302 Austenitic Stainless Steel, 1/2 Hardened Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Strength, Yield | 760 MPa | 110000 psi | |
| Elgiloy® Co-Cr-Ni Alloy, Wire, 10% Cold Reduction, Heat Treated Heat Treatment 5 hours at 527°C. The strength, shear modulus, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: Hi.. |
|||
| Tensile Strength, Yield | 760 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
| Carpenter Pyromet® CTX-3 Superalloy, Heat Treatment for Brazing Cycles over 982°C Data provided by Carpenter Technology Corporation.Pyromet® alloy CTX-3 is a high strength, precipitation hardenable superalloy which exhibits a low CTE over a broad temperature range. This alloy a.. |
|||
| Tensile Strength, Yield | 758 - 827 MPa @Strain 0.200 % |
110000 - 120000 psi @Strain 0.200 % |
|
| Ametek AM 388™ Alloy (UNS C72650) TX00 Information supplied by Ametek Specialty Metal Products Division.Copper base Spinodal alloy with high conductivity and high strength. Outstanding performance for contacts in connectors, sockets and.. |
|||
| Tensile Strength, Yield | 760 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
| ATI Allegheny Ludlum AL 17-4 High Strength Stainless Steel, UNS S17400 Property data below is typical of annealed samples. Available in plate. For use in fasteners, fittings, military equipment and air frame parts.Information provided by Allegheny Ludlum |
|||
| Tensile Strength, Yield | 759 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
| ATI Allegheny Ludlum Grade 23 (6-4 ELI) Titanium (UNS R56401) The ELI grade has lower impurity limits than standard titanium 6-4.Uses: applications requiring excellent fracture toughness and fatigue strength, aircraft, structural components, biomedical.Mechani.. |
|||
| Tensile Strength, Yield | 758 MPa @Strain 0.200 %, Temperature 538 °C |
110000 psi @Strain 0.200 %, Temperature 1000 °F |
|
| Carpenter Custom 455® Stainless Steel, Condition H950 (Age Hardened 510°C) Data provided by Carpenter Technology Corporation.Recognizing the need for high-strength alloys with good corrosion resistance to atmospheric environments, the Carpenter Research Laboratory develope.. |
|||
| Tensile Strength, Yield | 760 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
| ATI Allegheny Ludlum AL 15-5 High Strength Stainless Steel, UNS S15500 Property data below is typical of annealed samples. Available in plate. For use in fasteners, military equipment and air frame parts.Information provided by Allegheny Ludlum |
|||
| Tensile Strength, Yield | 758 MPa | 110000 psi | |
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 305, 30% Cold Rolled (UNS S30500) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
| Tensile Strength, Yield | 758 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
| ATI Allegheny Ludlum Stainless Steel Free Machining Grade Type 416, Tempered at 538°C (UNS S41600) Allegheny Ludlum's 416 is a free-machining stainless steel specifically designed to exhibit improved machinability. These modifications retain, in so far as possible, the good mechanical properties.. |
|||
| Tensile Strength, Yield | 760 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
| Carpenter BioDur™ CCM® Medical Implant Alloy, Hot Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur Carpenter CCM alloy.. |
|||
| Tensile Strength, Yield | 759 MPa @Treatment Temp. 760 °C, Time 360000 sec |
110000 psi @Treatment Temp. 1400 °F, Time 100 hour |
0.2%. Room temp test after thermal exposure |
| Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b.. |
|||