Carmel Olefins CAPILENE® QU 73 AV Propylene Random Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer Carmel Olefins
Trade Name CAPILENE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Carmel Olefins CAPILENE® QU 73 AV Propylene Random Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: CAPILENE® QU 73 AV is a high melt flow rate, controlled rheology polypropylene random copolymer for injection molding of clear articles. CAPILENE® QU 73 AV is clarified with antistatic additivation. It exhibits good organoleptic properties, good flowability combined with good impact strength at ambient temperature, low warpage and high transparency.Applications: CAPILENE® QU 73 AV is suitable for injection molding of transparent very thin walled items or those with complex geometry, household articles and clear packaging.Information provided by Carmel Olefins.
Physical Properties Metric English Comments
Melt Flow 38 g/10 min

@Load 2.16 kg,
Temperature 230 °C
38 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 25.0 MPa
3630 psi
50 mm/min; ASTM D638
Elongation at Yield 14 %
14 %
50 mm/min; ASTM D638
Flexural Modulus 1.05 GPa
152 ksi
ASTM D790
Izod Impact, Notched 0.500 J/cm
0.937 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 80.0 °C
176 °F
ASTM D648
Vicat Softening Point 130 °C

@Load 1.02 kg
266 °F

@Load 2.25 lb
ASTM D1525
Optical Properties Metric English Comments
Haze 8.0 %

@Thickness 1.00 mm
8.0 %

@Thickness 0.0394 in
ASTM D1003
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Processing Properties Metric English Comments
Melt Temperature 210 - 260 °C
410 - 500 °F
Mold Temperature 30.0 - 40.0 °C
86.0 - 104 °F