CP-Polymer-Technik Wellamid® 6000/50 CP Nylon 6, Impact Modified Until 0°C, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | CP-Polymer-Technik GmbH & Co. |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CP-Polymer-Technik Wellamid® 6000/50 CP Nylon 6, Impact Modified Until 0°C, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.5 - 3.3 % | 2.5 - 3.3 % | 23°C/50%RH, Starting when dry; DIN 53495 |
| Linear Mold Shrinkage | 0.0080 - 0.012 cm/cm @Thickness 4.00 mm |
0.0080 - 0.012 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 |
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 25 % | 25 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 1.00 GPa | 145 ksi | ISO 527 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 215 °C | 419 °F | Kofler |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | ISO 3915 |
| Dielectric Constant | 7.0 @Frequency 1e+6 Hz |
7.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 243-1 |
| Dielectric Loss Index | 0.30 | 0.30 | At 1 MHz; IEC 250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 245 - 260 °C | 473 - 500 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Holding Pressure | High | |
| Injection Speed | Medium | |
| Screw Speed | Medium |
Users viewing this material also viewed the following:
- MV Labs B900 BPO4 Boron phosphate
- Pyrotek Pyroboard™ S1200 Roller
- Type P-VSB-32 (Union Carbide) Carbon Fiber
- Kennametal Stellite Nistelle C22 Nickel Superalloy
- Fujipoly Industries Sarcon® 30GSR Thin-Film GSR
- Shakespeare Sanstat® CN125 .52mm Nylon 66 Monofilament
- Fainplast Compounds GS 59/C Flexible PVC, Injection Molding for Footwear
- TSE Industries EcoWIND® P200G High Performance Filament Winding Polyurethane Resin for Pipes
Copyright © lookpolymers.com All Rights Reserved