Borealis Visico™/Visico™ LE4423/LE4438 Polyethylene Compound, Crosslinkable

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Borealis
Trade Name Visico™/Visico™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Visico™/Visico™ LE4423/LE4438 Polyethylene Compound, Crosslinkable.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Visico™ LE4423 / Visico™ LE4438 is a silane crosslinkable natural compound designed for low voltage power cables up to 6 kV. Visico™ LE4423 and Visico™ LE4438 is a combination of a Visico™ base material and a catalyst master batch which accelerates the moisture-induced crosslinking reaction. When properly mixed, addition of 5 parts of Visico™ LE4438 to 95 parts of Visico™ LE4423, insulation with excellent thermo-oxidative stability, also in contact with copper as well as aluminum, is achieved. Applications: Insulation of low voltage cables for the range up to 6 kV. Additives: Visico™ LE4423 / Visico™ LE4438 contains antioxidant and metal deactivator. Visico™ LE4423 contains a permanent scorch retardant additive, ensuring safe processing and enabling the use of a highly active crosslinking catalyst. Specifications: Visico™ LE4423 / Visico™ LE4438 in combination meets the applicable requirements as below when processed using sound extrusion and testing procedure: ASTM D 1248 Type I, Class A, Category 4; IEC 60502-1; HD 603 S1; HD 604 S1; NEMA WC 70; and NEMA WC 71.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.923 g/cc
0.0333 lb/in³
mixture 95:5; ISO 1183/ISO 1872-2
Environmental Stress Crack Resistance >= 96 hour

@Temperature 50.0 °C
>= 96 hour

@Temperature 122 °F
Igepal 10%, F20; IEC 60811-4-1/B
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 52
52
1s; ISO 868
Tensile Strength at Break <= 11.25 MPa
<= 1632 psi
after aging (240h, 135°C); IEC 60811-1-2
>= 15.0 MPa
>= 2180 psi
250mm/min; ISO 527
Elongation at Break >= 300 %
>= 300 %
250mm/min; ISO 527
Thermal Properties Metric English Comments
Brittleness Temperature <= -76.0 °C
<= -105 °F
ASTM D746
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+6 ohm-cm
>= 1.00e+6 ohm-cm
IEC 60093
Dielectric Constant 2.3

@Frequency 50000 Hz
2.3

@Frequency 50000 Hz
IEC 60250
Dielectric Strength >= 22.0 kV/mm
>= 559 kV/in
IEC 60243
Dissipation Factor 0.00050

@Frequency 50000 Hz
0.00050

@Frequency 50000 Hz
IEC 60250
Processing Properties Metric English Comments
Zone 1 150 °C
302 °F
Zone 2 170 °C
338 °F
Zone 3 170 °C
338 °F
Zone 4 170 °C
338 °F
Die Temperature 170 °C
338 °F
Shelf Life 18.0 Month
18.0 Month
Descriptive Properties Value Comments
Hot Set Test, % 0
200°C, 0.2 MPa; IEC 60811-2-1; Permanent Deformation
60
200°C, 0.2 MPa;IEC 60811-2-1; Elongation under load