Borealis Borcoat™ HE3453 Natural High Density Polyethylene for Steel Pipe Coating

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer Borealis
Trade Name Borcoat™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Borcoat™ HE3453 Natural High Density Polyethylene for Steel Pipe Coating.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Borcoat HE3453 is a natural and colorable high density polyethylene produced with the Borstar technology in similar conditions as the black ready made top coat Borcoat HE3450. Borcoat HE3453 is recommended as colorable HDPE top-coat for yellow and blue coating system. Borcoat HE3453 can be used up to 80°C service temperature of the pipeline when combined with grafted adhesives either Borcoat ME0420 or Borcoat ME0433.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 0.942 g/cc
0.0340 lb/in³
Base Resin; ISO 1183/ISO 1872-2B
ESCR 10% Igepal® >= 5000 hour
>= 5000 hour
IEC 811-4-1/B, ASTM D1693-A
Melt Flow 0.50 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.50 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
2.0 g/10 min

@Load 5.00 kg,
Temperature 190 °C
2.0 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 60
60
ASTM D2240
Tensile Strength, Ultimate >= 26.0 MPa
>= 3770 psi
ASTM D638
Elongation at Break >= 600 %
>= 600 %
ASTM D638
Thermal Properties Metric English Comments
Melting Point >= 128 °C
>= 262 °F
ISO 3146
Vicat Softening Point 120 °C
248 °F
A50 (10 N); ISO 306
Brittleness Temperature <= -82.0 °C
<= -116 °F
ASTM D746
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D258
Dielectric Strength >= 30.0 kV/mm
>= 762 kV/in
IEC 244
Processing Properties Metric English Comments
Front Barrel Temperature 190 - 210 °C
374 - 410 °F
Die Temperature 190 - 210 °C
374 - 410 °F
Melt Temperature 220 - 240 °C
428 - 464 °F
Head Temperature 190 - 210 °C
374 - 410 °F