Perstorp Compounds 171 Urea-Formaldehyde w/ cellulose filler

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Urea Formaldehyde, Molded, Cellulose Filled
Manufacturer Perstorp Compounds
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Perstorp Compounds 171 Urea-Formaldehyde w/ cellulose filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Perstorp Compounds Inc.
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
DIN 53 464
Mechanical Properties Metric English Comments
Tensile Strength at Break >= 55.0 MPa
>= 7980 psi
ISO 178
Flexural Strength >= 100 MPa
>= 14500 psi
ISO 178
Charpy Impact, Notched >= 0.110 J/cm²
>= 0.524 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 130 °C
>= 266 °F
ISO 175
Deflection Temperature at 8.0 MPa >= 90.0 °C
>= 194 °F
ISO 175
Flammability, UL94 V-0
V-0
Oxygen Index >= 30 %
>= 30 %
ASTM D2863
Shrinkage 0.80 - 1.2 %
0.80 - 1.2 %
Post Shrinkage; DIN 53 464
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
DIN 53 483
Surface Resistance >= 1.00e+11 ohm
>= 1.00e+11 ohm
DIN 53 482
Dielectric Constant 5.0
5.0
DIN 53 483
Dissipation Factor <= 0.10

@Frequency 1000 Hz
 <= 0.10

@Frequency 1000 Hz
 tan delta; DIN 53 483
Comparative Tracking Index >= 600 V
>= 600 V
IEC 112
Descriptive Properties Value Comments
Glow Bar 960°C 180 sec passes
IEC 707
Water Absorption [mg] <250
DIN 53 495/23°C 96h