Beijing Chemical Industry KAIFA® 301-G15RF PBT Resin
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® 301-G15RF PBT Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% glass fiber reinforced, flame retardant, good toughness, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ASTM D790 |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 67.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz |
3.1 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm |
559 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.018 @Frequency 1e+6 Hz |
0.018 @Frequency 1e+6 Hz |
ASTM D150 |
| Comparative Tracking Index | 250 V @Thickness 3.20 mm |
250 V @Thickness 0.126 in |
ASTM D3638 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 225 - 255 °C | 437 - 491 °F | |
| Nozzle Temperature | 245 °C | 473 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
| Back Pressure | 8.00 - 18.0 MPa | 1160 - 2610 psi | |
| Screw Speed | <= 100 rpm | <= 100 rpm |
Users viewing this material also viewed the following:
- SABIC 218B Linear Low Density Polyethylene for Cast Film
- SK Chemicals SKYTHANE® US230 Magnetic Binder
- Suzhou Hipro Polymers Hiprolon® 11ESNNHL P40 Nylon, dry
- DuPont Elvaloy® HP441 Ethylene/N-Butyl Acrylate/Carbon Monoxide Copolymer
- A. Schulman POLYFORT™ FPP 3710 Glass Filled Homopolymer Polypropylene
- Dow Corning XIAMETER® PMCPOHX-4012 Polymer 6000CS
- DuPont™ Surlyn® PC100 Ionomer Resin, Highest Clarity, Sodium
- California Fine Wire Alloy 20-245 Precious Metal Alloy
- Austin Novel Materials Texalan® 498A Polyester-based TPU
- A. Schulman POLYBATCH™ Blue 40460/4 Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved