Beijing Chemical Industry KAIFA® 101 PBT Resin
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® 101 PBT Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced, good toughnessInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Water Absorption | 0.14 % | 0.14 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.012 - 0.022 cm/cm | 0.012 - 0.022 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm @Thickness 3.20 mm |
0.937 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Charpy Impact Unnotched | 4.20 J/cm² | 20.0 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
44.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.025 @Frequency 1e+6 Hz |
0.025 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Ensinger ENSITEP® PET Polyethylene Terephthalate - Extruded Products (discontinued **)
- Solvay TECHNYL® C 218 V 50 PA6, 50% glass fiber, Eh 50
- Silberline Silvex® 420-15-C
- Samsung Cheil Industries Infino® HN-1064 PC, Unreinforced FR
- Silon Taborex TA 1132 HD Chemically-Crosslinkable HDPE Compound
- Covestro Makrolon® 2858 Polycarbonate, Injection Grade
- Chi Mei Polylac® PA-765 ABS - Flame Retardant
- BASF Elastollan R 2001 20% Glass Filled TPUR
- Axiall 50898 Moldings & Extrusions Flexible PVC
Copyright © lookpolymers.com All Rights Reserved