SABIC MG500026 Linear Low Density Polyethylene for Compounding

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Compounding Resin
Manufacturer	SABIC
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC MG500026 Linear Low Density Polyethylene for Compounding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: MG500026 is a Linear Low Density Polyethylene grade with a narrow molecular weight distribution primarily suitable for compounding applications. It is in the powder form and has been designed to exhibit excellent flow properties with better low temperature toughness, stress crack resistance and high gloss.Typical Applications: MG500026 is recommended for carpet backing, metal coating and compounding for masterbatch production.Information provided by SABIC.

Physical Properties	Metric	English	Comments
Density	0.926 g/cc	0.0335 lb/in³	load density; ASTM D1505
ESCR 100% Igepal®	6.0 hour	6.0 hour	F50; ASTM D1693B
ESCR 10% Igepal®	3.0 hour	3.0 hour	F50; ASTM D1693B
Melt Flow	50 g/10 min @Load 2.16 kg, Temperature 190 °C	50 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	50	50	ASTM D2240
Tensile Strength at Break	8.00 MPa	1160 psi	ASTM D638
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D638
Elongation at Break	>= 350 %	>= 350 %	ASTM D638
Flexural Strength	8.00 MPa	1160 psi	ASTM D790
Flexural Modulus	0.200 GPa	29.0 ksi	ASTM D790
1% Secant Modulus	240 MPa	34800 psi	ASTM D638
Izod Impact, Notched	5.00 J/cm	9.37 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Vicat Softening Point	88.0 °C	190 °F	ASTM D1525
Brittleness Temperature	<= -75.0 °C	<= -103 °F	ASTM D746

Processing Properties	Metric	English	Comments
Mold Temperature	15.0 - 60.0 °C	59.0 - 140 °F
Injection Pressure	60.0 - 100 MPa	8700 - 14500 psi