- Barlog Plastics KEBATRON L1040G3 PPS, linear, 40% glass fiber reinforced
Barlog Plastics KEBATRON L1040G3 PPS, linear, 40% glass fiber reinforced
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBATRON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBATRON L1040G3 PPS, linear, 40% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPS-GF40Information provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Water Absorption | 0.020 % | 0.020 % | similar to ISO 62 test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527-1 |
| Elongation at Break | 1.5 % | 1.5 % | ISO 527-1 |
| Tensile Modulus | 14.5 GPa | 2100 ksi | ISO 527-1 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179-1eU |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C | 12.2 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 285 °C | 545 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL Registered; IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | PPS-GF40 |
Users viewing this material also viewed the following:
- SABIC PP 500P Polypropylene Homopolymer for Raffia Applications
- Industeel CLC 18.10 L General Purpose 18Cr-10Ni Austenitic Stainless Steel
- ChevronTexaco Transformer Oil
- Colorite Polymers MULTICHEM™ 8014 Vinyl-Urethane Blend
- Axiall Suprel® SVA 9420 Rigid PVC, Molding
- ATG s.r.l. IR Synthetic Polyisoprene
- Dow Corning 3-0135 Cosmetic Fluid
- E-Polymers EFLEX® S5050 Extrusion
- Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved