- Barlog Plastics KEBATER BM240 PBT, 40% mineral reinforced, food grade
Barlog Plastics KEBATER BM240 PBT, 40% mineral reinforced, food grade
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Mineral Filled |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBATER |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBATER BM240 PBT, 40% mineral reinforced, food grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
(PBT+X)-MD40Information provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.81 g/cc | 0.0654 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | similar to ISO 62 test |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4 |
| Melt Flow | 45 g/10 min @Load 2.16 kg, Temperature 260 °C |
45 g/10 min @Load 4.76 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ISO 527-1 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1 |
| Tensile Modulus | 4.00 GPa | 580 ksi | ISO 527-1 |
| Charpy Impact Unnotched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179-1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
UL Registered; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | (PBT+X)-MD40 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Z70M Hydrogenated NBR Compound
- Lehmann & Voss LUVOCOM® 1301-8400 PPS, linear, with carbon fiber, PTFE, lubricant modified
- H.C. Starck Amperit® 526.062 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17
- Mueller Alloy 3600 Free Cutting Brass (UNS C36000)
- Styron XZ 92069.01 Carboxylated SB
- Tipco Tipcolite® TPF 1911 - Cashew Nut (CNSL) Modified Phenolic Resin with 51 mm Norton Flow, with 7% Hexamine
- ChevronTexaco SAE 40 Military Symbol 9250 Engine Oil
- ChevronTexaco Delo® 100 Motor Oil, SAE 30
- Arlon P31000A005 0.005" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- ALM TPE-210-S Prototyping Polymer
Copyright © lookpolymers.com All Rights Reserved