BLUESTAR LXS 314 G40 PPE-HIPS, 40% Glass Filled
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Glass Filler |
| Manufacturer | BLUESTAR |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BLUESTAR LXS 314 G40 PPE-HIPS, 40% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Applications: Military industrial productsInformation provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Temperature 23.0 °C, Time 86400 sec |
0.10 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 300 °C |
12 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | type I; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | type I; ASTM D638 |
| Flexural Strength | 190 MPa | 27600 psi | 2.6 mm/min; ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | 2.6 mm/min; ASTM D790 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C @Thickness 6.40 mm |
293 °F @Thickness 0.252 in |
ASTM D648 |
Users viewing this material also viewed the following:
- RheTech Products HP506-01A 21% Talc Reinforced High Performance Polypropylene, UV Stabilized, Black
- Lanxess Durethan® DP AKV 50 HR H2.0 901510 Nylon 66, 50% Glass Fiber
- A. Schulman PP 2173-01 Polypropylene High-Impact Polypropylene
- Westlake Epolene® L630-29L Branched Low Density Polyethylene Homopolymer
- A. Schulman POLYBATCH™ Red 5670 Concentrate Based In Polyethylene
- DuPont Performance Polymers Rynite® FR530 BK507 Polyethylene Terephthalate (PET) (Unverified Data**)
- Ashley Polymers Ashlene® 745 Nylon 6/69
- Latrobe LSS™ S7 Shock-Resisting Tool Steel (ASTM S7)
- A. Schulman POLYFLAM™ FCB 1236-8555 General Purpose Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved