BLUESTAR 403G-MG30 PBT, 30% Glass Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | BLUESTAR |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BLUESTAR 403G-MG30 PBT, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Applications: High GWIT, RTI, E/EInformation provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.16 % | 0.16 % | 50% RH; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 250 °C |
19 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ASTM D638 |
| Flexural Strength | 175 MPa | 25400 psi | ASTM D790 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m² | 30.9 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
||
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Glow Wire Test | 750 °C | 1380 °F | GWIT |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.30e+16 ohm-cm | 1.30e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Nabaltec GRANALOX® NM 9212 E Ceramic Bodies
- Premix Thermoplastics PRE-ELEC® ESD 6300 Static Dissipative Thermoplastic Compound
- Lotte Chemical Titan TITANPRO® PM200 Polypropylene homopolymer
- SABIC Innovative Plastics NORYL SE1GFN3 PPE+HIPS (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP QC006I PA 6/10
- SABIC Innovative Plastics LNP THERMOTUF QX01581H PA6.10
- Unipetrol P II Propane
- Chesterton ARC 5ES Rapid Repair Stick
- Chevron Phillips Marlex® B592 Polyethylene, Injection Molding Grade, HDPE (discontinued **)
- Solvay Specialty Polymers Amodel® HFZ A-1133 L Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved