Americas Styrenics STYRON® 610 High Heat Crystal Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Heat Resistant Grade |
| Manufacturer | Americas Styrenics LLC |
| Trade Name | STYRON® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Americas Styrenics STYRON® 610 High Heat Crystal Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product CharacteristicsAdditive freeTypical ApplicationsFoamsFilms/opticalCarrier resinSpecialty blendingInformation provided by AmericasStyrenics LLC.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 200 °C |
10 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 110 | 110 | ASTM D785 |
| Tensile Strength at Break | 44.1 MPa | 6400 psi | ASTM D638 |
| Tensile Strength | 44.1 MPa | 6400 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ASTM D638 |
| Flexural Strength | 62.1 MPa | 9000 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.214 J/cm | 0.400 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 96.7 °C | 206 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.3 °C | 191 °F | ASTM D648 |
| Vicat Softening Point | 107 °C | 225 °F | ASTM D1525 |
Users viewing this material also viewed the following:
- Palm Labs Adhesives TURBO FUSE SERIES 190-HT (4000 cp HIGH TEMPERATURE) Rapid Bonding Adhesive
- Parker Chomerics Tecknit Consil®-C 873 Silver-Copper Filled Silicone Elastomer
- Overview of materials for Nylon 66, Stainless Steel Filled; EMI Grade
- Minelco Muscovite Mica
- SABIC Innovative Plastics LNP THERMOCOMP JF006LXZ PES
- Samyang Tramid® 210G35 Polyamide, Reinforced
- Lubrizol Estane® ALR E77A-V Thermoplastic Polyurethane
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Atomite Whiting Filler
- ELASTO UK Dryflex® 3021-001 TPE, Modified Injection Molding Grade for Sanitary Seals
- Axiall 15643 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved